Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| melt mass-flow rate | | ASTM D1238 | 5.0 g/10min |
| melt mass-flow rate | | ISO 1133 | 5.0 g/10min |
| IonType | | | Zinc |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Shore hardness | | ASTM D2240 | 63 |
| Shore hardness | | ISO 868 | 63 |
| optical performance | Test Condition | Test Method | Test Result |
|---|
| Haze ratio | | ASTM D1003 | 27 % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile strain | | ISO 527-2 | 410 % |
| Flexural modulus | | ASTM D790 | 680 Mpa |
| Flexural modulus | | ASTM D790 | 220 Mpa |
| wear resistance | | ASTM D1630 | 270 |
| tensile strength | | ASTM D638 | 12.4 Mpa |
| tensile strength | | ASTM D638 | 22.1 Mpa |
| tensile strength | | ISO 527-2 | 22.1 Mpa |
| elongation | | ASTM D638 | 410 % |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ASTM D1822 | 893 kJ/m² |
| Impact strength of cantilever beam gap | | ASTM D1822 | 967 kJ/m² |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| brittle temperature | | ASTM D746 | -80.0 °C |
| vicat | | ASTM D1525 | 71.0 °C |
| vicat | | ISO 306 | 71.0 °C |
| melting temperature | | ASTM D3418 | 92.0 °C |
| melting temperature | | ISO 3146 | 92.0 °C |
| Linear coefficient of thermal expansion | | ASTM D696 | 1.5E-04 cm/cm/°C |
| FreezingPoint | | ASTM D3418 | 73 °C |
| FreezingPoint | | ISO 3146 | 73 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.