Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
SURLYN 9650 DUPONT USA
Surlyn®
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | DUPONT USA/9650 |
|---|---|---|---|
| Impact strength of cantilever beam gap | 23°C | ASTM D1822 | 967 kJ/m² |
| -40°C | ASTM D1822 | 893 kJ/m² |
| hardness | Test Condition | Test Method | DUPONT USA/9650 |
|---|---|---|---|
| Shore hardness | 邵氏D | ASTM D2240 | 63 |
| 邵氏D | ISO 868 | 63 |
| Mechanical properties | Test Condition | Test Method | DUPONT USA/9650 |
|---|---|---|---|
| Flexural modulus | -20°C | ASTM D790 | 680 Mpa |
| Tensile strain | 断裂,23°C | ISO 527-2 | 410 % |
| wear resistance | NBS指数 | ASTM D1630 | 270 |
| tensile strength | Yield,23°C,CompressionMolded | ASTM D638 | 12.4 Mpa |
| 断裂,23°C | ISO 527-2 | 22.1 Mpa | |
| 断裂,23°C | ASTM D638 | 22.1 Mpa | |
| Flexural modulus | 23°C | ASTM D790 | 220 Mpa |
| elongation | 断裂,23°C | ASTM D638 | 410 % |
| optical performance | Test Condition | Test Method | DUPONT USA/9650 |
|---|---|---|---|
| Haze ratio | 6350µm | ASTM D1003 | 27 % |
| physical property | Test Condition | Test Method | DUPONT USA/9650 |
|---|---|---|---|
| IonType | Zinc | ||
| melt mass-flow rate | 190°C/2.16kg | ASTM D1238 | 5.0 g/10min |
| 190°C/2.16kg | ISO 1133 | 5.0 g/10min |
| Thermal performance | Test Condition | Test Method | DUPONT USA/9650 |
|---|---|---|---|
| vicat | ASTM D1525 | 71.0 °C | |
| ISO 306 | 71.0 °C | ||
| Linear coefficient of thermal expansion | MD：-20to32°C | ASTM D696 | 1.5E-04 cm/cm/°C |
| brittle temperature | ASTM D746 | -80.0 °C | |
| melting temperature | ASTM D3418 | 92.0 °C | |
| FreezingPoint | -- | ISO 3146 | 73 °C |
| -- | ASTM D3418 | 73 °C | |
| melting temperature | ISO 3146 | 92.0 °C |