PPO(PPE)+PS+PP NORYL PPX™ PPX630F resin
0
- Properties:Fillerglass fiber reinforced material30%filler by weight
CompareTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Shrinkage rate | 内部方法 | 0.25to0.76 % | |
| density | ASTM D792 | 1.19 g/cm³ | |
| melt mass-flow rate | ASTM D1238 | 2.6 g/10min | |
| Shrinkage rate | 内部方法 | 0.20to0.23 % |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | UL 94 | HB |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Impact strength of cantilever beam gap | ASTM D256 | 100 J/m | |
| ASTM D256 | 170 J/m | ||
| ASTM D4812 | 830 J/m | ||
| Dart impact | ASTM D3763 | 20.4 J | |
| ASTM D3763 | 19.1 J |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| tensile strength | Yield | ASTM D638 | 79.3 MPa |
| Break | ASTM D638 | 79.3 MPa | |
| elongation | Break | ASTM D638 | 7.7 % |
| Flexural modulus | ASTM D790 | 5560 MPa | |
| bending strength | ASTM D790 | 130 MPa |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Linear coefficient of thermal expansion | ASTME831 | 7.7E-05 cm/cm/°C | |
| Heat distortion temperature | ASTM D648 | 155 °C | |
| ASTM D648 | 134 °C | ||
| vicat | ASTM D15254 | 162 °C | |
| Linear coefficient of thermal expansion | ASTME831 | 1.4E-05 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.