PPO(PPE)+PS+PP NORYL PPX™ PPX630F resin SABIC
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC/NORYL PPX™ PPX630F resin |
|---|---|---|---|
| Impact strength of cantilever beam gap | -30°C | ASTM D256 | 100 J/m |
| 23°C | ASTM D256 | 170 J/m | |
| Dart impact | 23°C,TotalEnergy | ASTM D3763 | 19.1 J |
| -30°C,TotalEnergy | ASTM D3763 | 20.4 J | |
| Impact strength of cantilever beam gap | 23°C | ASTM D4812 | 830 J/m |
| Mechanical properties | Test Condition | Test Method | SABIC/NORYL PPX™ PPX630F resin |
|---|---|---|---|
| elongation | 断裂 | ASTM D638 | 7.7 % |
| bending strength | Break,50.0mmSpan | ASTM D790 | 130 MPa |
| tensile strength | 断裂 | ASTM D638 | 79.3 MPa |
| 屈服 | ASTM D638 | 79.3 MPa | |
| Flexural modulus | 50.0mm跨距 | ASTM D790 | 5560 MPa |
| flammability | Test Condition | Test Method | SABIC/NORYL PPX™ PPX630F resin |
|---|---|---|---|
| UL flame retardant rating | 1.5mm | UL 94 | HB |
| physical property | Test Condition | Test Method | SABIC/NORYL PPX™ PPX630F resin |
|---|---|---|---|
| Shrinkage rate | MD：3.20mm | 内部方法 | 0.20to0.23 % |
| melt mass-flow rate | 260°C/5.0kg | ASTM D1238 | 2.6 g/10min |
| Shrinkage rate | TD：3.20mm | 内部方法 | 0.25to0.76 % |
| density | ASTM D792 | 1.19 g/cm³ |
| Thermal performance | Test Condition | Test Method | SABIC/NORYL PPX™ PPX630F resin |
|---|---|---|---|
| Linear coefficient of thermal expansion | TD：-40到40°C | ASTME831 | 7.7E-05 cm/cm/°C |
| vicat | ASTM D15254 | 162 °C | |
| Heat distortion temperature | 0.45MPa,未退火,3.20mm，HDT | ASTM D648 | 155 °C |
| Linear coefficient of thermal expansion | MD：-40到40°C | ASTME831 | 1.4E-05 cm/cm/°C |
| Heat distortion temperature | 1.8MPa,未退火,3.20mm，HDT | ASTM D648 | 134 °C |