ABS/PC CYCOLOY™ CX7240-7M1D218
799
- Properties:Flame retardantHigh impact resistanceHigh mobility
- Usages:Electrical fieldElectronic fieldConstruction fieldOutdoor applicationsEngine hood partsMedical suppliesNursing suppliesPlastic bagCastersAerospace ApplicationsLiquid handling
Compare
View PricesTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| melt mass-flow rate | ASTM D1238 | 18 g/10 min | |
| Melt volume flow rate | ISO 1133 | 15.0 cm3/10min | |
| Shrinkage rate | 内部方法 | 0.40 - 0.60 % | |
| Water absorption rate | ISO 62 | 0.20 % | |
| ISO 62 | 0.10 % |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | UL 94 | V-1 | |
| UL 94 | V-0 | ||
| UL 94 | 5VB | ||
| UL 94 | 5VA | ||
| Burning wire flammability index | IEC 60695-2-12 | 960 °C | |
| IEC 60695-2-12 | 960 °C | ||
| Hot filament ignition temperature | IEC 60695-2-13 | 775 °C | |
| IEC 60695-2-13 | 825 °C | ||
| IEC 60695-2-13 | 775 °C | ||
| IEC 60695-2-13 | 800 °C | ||
| IEC 60695-2-13 | 775 °C | ||
| Limiting Oxygen Index | ISO 4589-2 | 34 % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile modulus | ASTM D638 | 2600 Mpa | |
| ISO 527-2/1 | 2600 Mpa | ||
| tensile strength | ASTM D638 | 65.0 Mpa | |
| ISO 527-2/50 | 65.0 Mpa | ||
| ASTM D638 | 58.0 Mpa | ||
| ISO 527-2/50 | 50.0 Mpa | ||
| elongation | ASTM D638 | 4.1 % | |
| ISO 527-2/50 | 4.0 % | ||
| ASTM D638 | 100 % | ||
| ISO 527-2/50 | 90 % | ||
| Flexural modulus | ASTM D790 | 2500 Mpa | |
| ISO 178 | 2500 Mpa | ||
| bending strength | ISO 178 | 96.0 Mpa | |
| ASTM D790 | 104 Mpa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Dart impact | ASTM D3763 | 65.0 J |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Surface Resistivity | IEC 60093 | > 1.0E+15 ohms | |
| Volume resistivity | IEC 60093 | > 1.0E+15 ohms·cm | |
| dielectric strength | IEC 60243-1 | 35 KV/mm | |
| IEC 60243-1 | 25 KV/mm | ||
| IEC 60243-1 | 17 KV/mm | ||
| Compared to the Leakage Tracking Index (CTI) | UL 746 | PLC 3 | |
| High arc combustion index (HAI) | UL 746 | PLC 0 | |
| Hot wire ignition (HWI) | UL 746 | PLC 3 |
| injection | Test Condition | Test Method | Test Result |
|---|---|---|---|
| drying temperature | 80 to 90 °C | ||
| drying time | 2.0 to 4.0 hr | ||
| Suggested maximum moisture content | 0.020 % | ||
| Hopper temperature | 60 to 80 °C | ||
| Temperature at the rear of the barrel | 230 to 280 °C | ||
| Temperature in the middle of the barrel | 240 to 290 °C | ||
| Temperature at the front of the material cylinder | 250 to 300 °C | ||
| Spray nozzle temperature | 250 to 300 °C | ||
| Processing (melt) temperature | 250 to 300 °C | ||
| Temperature | 60 to 85 °C | ||
| Exhaust hole depth | 0.030 to 0.075 mm |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat distortion temperature | ASTM D648 | 100 °C | |
| ASTM D648 | 89.0 °C | ||
| ASTM D648 | 99.0 °C | ||
| ISO 75-2/Af | 93.0 °C | ||
| vicat | ASTM D152511 | 110 °C | |
| ISO 306/B120 | 113 °C | ||
| ball-indentation hardness | IEC 60695-10-2 | 通过 | |
| Linear coefficient of thermal expansion | ASTM E831 | 7.5E-5 cm/cm/°C | |
| ASTM E831 | 7.5E-5 cm/cm/°C | ||
| ISO 11359-2 | 7.5E-5 cm/cm/°C | ||
| thermal conductivity | ISO 8302 | 0.20 W/m/K | |
| RTI Elec | UL 746 | 90.0 °C | |
| RTI Imp | UL 746 | 90.0 °C | |
| RTI | UL 746 | 90.0 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.