Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
ABS/PC CX7240-7M1D218 SABIC INNOVATIVE NANSHA
CYCOLOY™
Electrical field、Electronic field、Construction field、Outdoor applications、Engine hood parts、Medical supplies、Nursing supplies、Plastic bag、Casters、Aerospace Applications、Liquid handling
Flame retardant、High impact resistance、High mobility
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/CX7240-7M1D218 |
|---|---|---|---|
| Dart impact | 23°C, Total Energy | ASTM D3763 | 65.0 J |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/CX7240-7M1D218 |
|---|---|---|---|
| Tensile modulus | --2 | ASTM D638 | 2600 Mpa |
| tensile strength | 屈服3 | ASTM D638 | 65.0 Mpa |
| elongation | 断裂3 | ASTM D638 | 100 % |
| 断裂 | ISO 527-2/50 | 90 % | |
| Flexural modulus | --5 | ISO 178 | 2500 Mpa |
| bending strength | 屈服, 50.0 mm 跨距4 | ASTM D790 | 104 Mpa |
| --5,6 | ISO 178 | 96.0 Mpa | |
| Flexural modulus | 50.0 mm 跨距4 | ASTM D790 | 2500 Mpa |
| tensile strength | 断裂 | ISO 527-2/50 | 50.0 Mpa |
| 屈服 | ISO 527-2/50 | 65.0 Mpa | |
| elongation | 屈服 | ISO 527-2/50 | 4.0 % |
| 屈服3 | ASTM D638 | 4.1 % | |
| tensile strength | 断裂3 | ASTM D638 | 58.0 Mpa |
| Tensile modulus | -- | ISO 527-2/1 | 2600 Mpa |
| Electrical performance | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/CX7240-7M1D218 |
|---|---|---|---|
| dielectric strength | 1.60 mm, 在油中 | IEC 60243-1 | 25 KV/mm |
| Volume resistivity | IEC 60093 | > 1.0E+15 ohms·cm | |
| dielectric strength | 0.800 mm, 在油中 | IEC 60243-1 | 35 KV/mm |
| Hot wire ignition (HWI) | UL 746 | PLC 3 | |
| Compared to the Leakage Tracking Index (CTI) | UL 746 | PLC 3 | |
| Surface Resistivity | IEC 60093 | > 1.0E+15 ohms | |
| dielectric strength | 3.20 mm, 在油中 | IEC 60243-1 | 17 KV/mm |
| High arc combustion index (HAI) | UL 746 | PLC 0 |
| flammability | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/CX7240-7M1D218 |
|---|---|---|---|
| UL flame retardant rating | 3.0 mm | UL 94 | 5VA |
| Hot filament ignition temperature | 1.5 mm13 | IEC 60695-2-13 | 775 °C |
| UL flame retardant rating | 0.60 mm | UL 94 | V-1 |
| Burning wire flammability index | 0.75 mm | IEC 60695-2-12 | 960 °C |
| Hot filament ignition temperature | 3.0 mm | IEC 60695-2-13 | 800 °C |
| UL flame retardant rating | 0.75 mm | UL 94 | V-0 |
| Burning wire flammability index | 0.75 mm13 | IEC 60695-2-12 | 960 °C |
| Hot filament ignition temperature | 1.0 mm | IEC 60695-2-13 | 825 °C |
| UL flame retardant rating | 1.5 mm | UL 94 | 5VB |
| Hot filament ignition temperature | 0.75 mm13 | IEC 60695-2-13 | 775 °C |
| Limiting Oxygen Index | ISO 4589-2 | 34 % | |
| Hot filament ignition temperature | 3.0 mm13 | IEC 60695-2-13 | 775 °C |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/CX7240-7M1D218 |
|---|---|---|---|
| Water absorption rate | 平衡, 23°C, 50% RH | ISO 62 | 0.10 % |
| Melt volume flow rate | 260°C/2.16 kg | ISO 1133 | 15.0 cm3/10min |
| melt mass-flow rate | 260°C/2.16 kg | ASTM D1238 | 18 g/10 min |
| Water absorption rate | 饱和, 23°C | ISO 62 | 0.20 % |
| Shrinkage rate | 3.20 mm，Flow | 内部方法 | 0.40 - 0.60 % |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/CX7240-7M1D218 |
|---|---|---|---|
| Linear coefficient of thermal expansion | 流动 : -40 到 40°C | ASTM E831 | 7.5E-5 cm/cm/°C |
| vicat | -- | ASTM D152511 | 110 °C |
| Linear coefficient of thermal expansion | 横向 : -40°C | ISO 11359-2 | 7.5E-5 cm/cm/°C |
| Heat distortion temperature | 0.45 MPa, 未退火, 3.20 mm，HDT | ASTM D648 | 100 °C |
| RTI | UL 746 | 90.0 °C | |
| vicat | -- | ISO 306/B120 | 113 °C |
| thermal conductivity | ISO 8302 | 0.20 W/m/K | |
| ball-indentation hardness | 73 到 77°C | IEC 60695-10-2 | 通过 |
| Heat distortion temperature | 1.8 MPa, 未退火, 6.40 mm，HDT | ASTM D648 | 99.0 °C |
| RTI Imp | UL 746 | 90.0 °C | |
| Linear coefficient of thermal expansion | 横向 : -40 到 40°C | ASTM E831 | 7.5E-5 cm/cm/°C |
| Heat distortion temperature | 1.8 MPa, 未退火, 3.20 mm，HDT | ASTM D648 | 89.0 °C |
| 1.8 MPa, 未退火, 4.00 mm, 64.0 mm 跨距10，HDT | ISO 75-2/Af | 93.0 °C | |
| RTI Elec | UL 746 | 90.0 °C |
| injection | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/CX7240-7M1D218 |
|---|---|---|---|
| drying time | 2.0 to 4.0 hr | ||
| Suggested maximum moisture content | 0.020 % | ||
| Temperature in the middle of the barrel | 240 to 290 °C | ||
| Temperature at the rear of the barrel | 230 to 280 °C | ||
| Processing (melt) temperature | 250 to 300 °C | ||
| Exhaust hole depth | 0.030 to 0.075 mm | ||
| Hopper temperature | 60 to 80 °C | ||
| drying temperature | 80 to 90 °C | ||
| Temperature at the front of the material cylinder | 250 to 300 °C | ||
| Temperature | 60 to 85 °C | ||
| Spray nozzle temperature | 250 to 300 °C |