Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Shrinkage rate | | ISO 294-4 | 0.90 % |
| Shrinkage rate | | ISO 294-4 | 0.40 % |
| Water absorption rate | | ISO 62 | 0.90 % |
| Water absorption rate | | ISO 62 | 1.9 % |
| flammability | Test Condition | Test Method | Test Result |
|---|
| burning rate | | ISO 3795 | 0.0 mm/min |
| UL flame retardant rating | | UL 94 | HB |
| UL flame retardant rating | | UL 94 | HB |
| UL flame retardant rating | | UL 94 | HB |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ISO 527-2 | 10000 Mpa |
| Tensile stress | | ISO 527-2 | 195 Mpa |
| Tensile strain | | ISO 527-2 | 3.0 % |
| Flexural modulus | | ISO 178 | 9600 Mpa |
| Bending stress | | ISO 178 | 270 Mpa |
| Poisson's Ratio | | ISO 527 | 0.40 |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of simply supported beam without notch | | ISO 179 | 65 kJ/m² |
| Impact strength of simply supported beam without notch | | ISO 179 | 75 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Volume resistivity | | IEC 60093 | 1.0E+13 ohms·cm |
| dielectric strength | | IEC 60243 | 24 KV/mm |
| arc resistance | | ASTM D495 | 5.00 sec |
| CTI | | IEC 60112 | 600 V |
| High arc combustion index (HAI) | | UL 746 | PLC 0 |
| High arc combustion index (HAI) | | UL 746 | PLC 0 |
| High arc combustion index (HAI) | | UL 746 | PLC 0 |
| High Voltage Arc Traceability Rate (HVTR) | | UL 746 | PLC 1 |
| Hot wire ignition (HWI) | | UL 746 | PLC 4 |
| Hot wire ignition (HWI) | | UL 746 | PLC 4 |
| Hot wire ignition (HWI) | | UL 746 | PLC 4 |
| injection | Test Condition | Test Method | Test Result |
|---|
| drying temperature | | | 80 °C |
| drying time | | | 4.0 hr |
| Suggested maximum recycled material ratio | | | 25 % |
| Temperature at the rear of the barrel | | | 280 到 310 °C |
| Temperature in the middle of the barrel | | | 280 到 310 °C |
| Temperature at the front of the material cylinder | | | 280 到 310 °C |
| Spray nozzle temperature | | | 280 到 310 °C |
| Processing (melt) temperature | | | 285 到 305 °C |
| Temperature | | | 65 到 95 °C |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ISO 75-2/B | 260 °C |
| Heat distortion temperature | | ISO 75-2/A | 250 °C |
| melting temperature | | ISO 11357-3 | 260 °C |
| | ISO 11359-2 | 2.2E-5 cm/cm/°C |
| | ISO 11359-2 | 1.1E-4 cm/cm/°C |
| RTI Elec | | UL 746 | 120 °C |
| RTI Elec | | UL 746 | 120 °C |
| RTI Elec | | UL 746 | 120 °C |
| RTI Imp | | UL 746 | 85.0 °C |
| RTI Imp | | UL 746 | 85.0 °C |
| RTI Imp | | UL 746 | 105 °C |
| RTI | | UL 746 | 115 °C |
| RTI | | UL 746 | 120 °C |
| RTI | | UL 746 | 120 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.