Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA66 R530J NT0724 ASCEND USA
Vydyne®
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | ASCEND USA/R530J NT0724 |
|---|---|---|---|
| Impact strength of simply supported beam without notch | -30°C | ISO 179 | 65 kJ/m² |
| 23°C | ISO 179 | 75 kJ/m² |
| Mechanical properties | Test Condition | Test Method | ASCEND USA/R530J NT0724 |
|---|---|---|---|
| Tensile strain | 断裂, 23°C | ISO 527-2 | 3.0 % |
| Poisson's Ratio | 23°C | ISO 527 | 0.40 |
| Flexural modulus | 23°C | ISO 178 | 9600 Mpa |
| Bending stress | 23°C | ISO 178 | 270 Mpa |
| Tensile modulus | 23°C | ISO 527-2 | 10000 Mpa |
| Tensile stress | 断裂, 23°C | ISO 527-2 | 195 Mpa |
| Electrical performance | Test Condition | Test Method | ASCEND USA/R530J NT0724 |
|---|---|---|---|
| Volume resistivity | 0.750 mm | IEC 60093 | 1.0E+13 ohms·cm |
| dielectric strength | 1.00 mm | IEC 60243 | 24 KV/mm |
| High arc combustion index (HAI) | 3.0 mm | UL 746 | PLC 0 |
| Hot wire ignition (HWI) | 0.75 mm | UL 746 | PLC 4 |
| High arc combustion index (HAI) | 0.75 mm | UL 746 | PLC 0 |
| Hot wire ignition (HWI) | 1.5 mm | UL 746 | PLC 4 |
| arc resistance | 3.00 mm | ASTM D495 | 5.00 sec |
| CTI | 3.00 mm | IEC 60112 | 600 V |
| Hot wire ignition (HWI) | 3.0 mm | UL 746 | PLC 4 |
| High Voltage Arc Traceability Rate (HVTR) | UL 746 | PLC 1 | |
| High arc combustion index (HAI) | 1.5 mm | UL 746 | PLC 0 |
| flammability | Test Condition | Test Method | ASCEND USA/R530J NT0724 |
|---|---|---|---|
| UL flame retardant rating | 3.0 mm | UL 94 | HB |
| burning rate | 2.00 mm, 自动灭火 | ISO 3795 | 0.0 mm/min |
| UL flame retardant rating | 0.75 mm | UL 94 | HB |
| 1.5 mm | UL 94 | HB |
| physical property | Test Condition | Test Method | ASCEND USA/R530J NT0724 |
|---|---|---|---|
| Water absorption rate | 平衡, 23°C, 50% RH | ISO 62 | 1.9 % |
| Shrinkage rate | 横向流量 : 23°C, 2.00 mm | ISO 294-4 | 0.90 % |
| 流量 : 23°C, 2.00 mm | ISO 294-4 | 0.40 % | |
| Water absorption rate | 24 hr, 23°C | ISO 62 | 0.90 % |
| Thermal performance | Test Condition | Test Method | ASCEND USA/R530J NT0724 |
|---|---|---|---|
| RTI Elec | 0.75 mm | UL 746 | 120 °C |
| Heat distortion temperature | 0.45 MPa, 未退火 | ISO 75-2/B | 260 °C |
| 横向 : 23 到 55°C, 2.00 mm | ISO 11359-2 | 1.1E-4 cm/cm/°C | |
| RTI | 0.75 mm | UL 746 | 115 °C |
| RTI Imp | 3.0 mm | UL 746 | 105 °C |
| RTI Elec | 1.5 mm | UL 746 | 120 °C |
| melting temperature | ISO 11357-3 | 260 °C | |
| RTI Imp | 0.75 mm | UL 746 | 85.0 °C |
| RTI | 3.0 mm | UL 746 | 120 °C |
| 流动 : 23 到 55°C, 2.00 mm | ISO 11359-2 | 2.2E-5 cm/cm/°C | |
| RTI Elec | 3.0 mm | UL 746 | 120 °C |
| Heat distortion temperature | 1.8 MPa, 未退火 | ISO 75-2/A | 250 °C |
| RTI Imp | 1.5 mm | UL 746 | 85.0 °C |
| RTI | 1.5 mm | UL 746 | 120 °C |
| injection | Test Condition | Test Method | ASCEND USA/R530J NT0724 |
|---|---|---|---|
| Temperature | 65 到 95 °C | ||
| Temperature at the rear of the barrel | 280 到 310 °C | ||
| Processing (melt) temperature | 285 到 305 °C | ||
| drying temperature | 80 °C | ||
| Temperature at the front of the material cylinder | 280 到 310 °C | ||
| drying time | 4.0 hr | ||
| Suggested maximum recycled material ratio | 25 % | ||
| Spray nozzle temperature | 280 到 310 °C | ||
| Temperature in the middle of the barrel | 280 到 310 °C |