Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ASTM D792 | 1.28 g/cm³ |
| Shrinkage rate | | ASTM D955 | 0.40 % |
| Shrinkage rate | | ASTM D955 | 0.40 % |
| Shrinkage rate | | ISO 294-4 | 0.40 % |
| Shrinkage rate | | ISO 294-4 | 0.39 % |
| Water absorption rate | | ASTM D570 | 0.11 % |
| Water absorption rate | | ISO 62 | 0.14 % |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | V-0 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ASTM D638 | 3450 MPa |
| Tensile modulus | | ISO 527-2/1 | 3750 MPa |
| bending strength | | ASTM D790 | 117 MPa |
| bending strength | | ISO 178 | 103 MPa |
| tensile strength | Break | ASTM D638 | 64.3 MPa |
| tensile strength | Break | ISO 527-2 | 64.6 MPa |
| elongation | Break | ASTM D638 | 3.7 % |
| Tensile strain | Break | ISO 527-2 | 3.2 % |
| Flexural modulus | | ASTM D790 | 3520 MPa |
| Flexural modulus | | ISO 178 | 3520 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ASTM D256 | 23 J/m |
| Impact strength of cantilever beam gap | | ISO 180/1A | 2.4 kJ/m² |
| Impact strength of cantilever beam gap | | ASTM D4812 | 550 J/m |
| Suspended wall beam without notch impact strength | | ISO 180/1U | 37 kJ/m² |
| Dart impact | | ASTM D3763 | 1.93 J |
| Multi axis Instrumented Impact Energy | | ISO 6603-2 | 0.700 J |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Surface Resistivity | | ASTM D257 | 1.0E+2to1.0E+6 ohms |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Linear coefficient of thermal expansion | | ASTME831 | 5.2E-05 cm/cm/°C |
| Linear coefficient of thermal expansion | | ISO 11359-2 | 5.2E-05 cm/cm/°C |
| Linear coefficient of thermal expansion | | ASTME831 | 5.2E-05 cm/cm/°C |
| Linear coefficient of thermal expansion | | ISO 11359-2 | 5.2E-05 cm/cm/°C |
| Heat distortion temperature | | ASTM D648 | 86.7 °C |
| Heat distortion temperature | | ISO 75-2/Bf | 88.4 °C |
| Heat distortion temperature | | ASTM D648 | 82.2 °C |
| Heat distortion temperature | | ISO 75-2/Af | 82.0 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.