PC LNP™ STAT-KON™ DD0001 compound SABIC
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC/LNP™ STAT-KON™ DD0001 compound |
|---|---|---|---|
| Suspended wall beam without notch impact strength | 23°C | ISO 180/1U | 37 kJ/m² |
| Impact strength of cantilever beam gap | 23°C | ASTM D256 | 23 J/m |
| Multi axis Instrumented Impact Energy | ISO 6603-2 | 0.700 J | |
| Impact strength of cantilever beam gap | 23°C | ASTM D4812 | 550 J/m |
| 23°C | ISO 180/1A | 2.4 kJ/m² | |
| Dart impact | 23°C,EnergyatPeakLoad | ASTM D3763 | 1.93 J |
| Electrical performance | Test Condition | Test Method | SABIC/LNP™ STAT-KON™ DD0001 compound |
|---|---|---|---|
| Surface Resistivity | ASTM D257 | 1.0E+2to1.0E+6 ohms |
| Mechanical properties | Test Condition | Test Method | SABIC/LNP™ STAT-KON™ DD0001 compound |
|---|---|---|---|
| elongation | 断裂 | ASTM D638 | 3.7 % |
| Tensile modulus | ASTM D638 | 3450 MPa | |
| tensile strength | 断裂 | ASTM D638 | 64.3 MPa |
| 断裂 | ISO 527-2 | 64.6 MPa | |
| Tensile strain | 断裂 | ISO 527-2 | 3.2 % |
| Flexural modulus | ASTM D790 | 3520 MPa | |
| bending strength | ASTM D790 | 117 MPa | |
| Flexural modulus | ISO 178 | 3520 MPa | |
| Tensile modulus | ISO 527-2/1 | 3750 MPa | |
| bending strength | ISO 178 | 103 MPa |
| flammability | Test Condition | Test Method | SABIC/LNP™ STAT-KON™ DD0001 compound |
|---|---|---|---|
| UL flame retardant rating | 1.7mm | UL 94 | V-0 |
| physical property | Test Condition | Test Method | SABIC/LNP™ STAT-KON™ DD0001 compound |
|---|---|---|---|
| Shrinkage rate | MD:24小时 | ISO 294-4 | 0.39 % |
| MD：24小时 | ASTM D955 | 0.40 % | |
| Water absorption rate | 24hr,50%RH | ASTM D570 | 0.11 % |
| 平衡,23°C,50%RH | ISO 62 | 0.14 % | |
| density | ASTM D792 | 1.28 g/cm³ | |
| Shrinkage rate | TD：24hr | ASTM D955 | 0.40 % |
| TD:24小时 | ISO 294-4 | 0.40 % |
| Thermal performance | Test Condition | Test Method | SABIC/LNP™ STAT-KON™ DD0001 compound |
|---|---|---|---|
| Heat distortion temperature | 0.45MPa,Unannealed,64.0mmSpan，HDT | ISO 75-2/Bf | 88.4 °C |
| Linear coefficient of thermal expansion | TD：-40到40°C | ASTME831 | 5.2E-05 cm/cm/°C |
| TD：-40到40°C | ISO 11359-2 | 5.2E-05 cm/cm/°C | |
| MD：-40到40°C | ASTME831 | 5.2E-05 cm/cm/°C | |
| Heat distortion temperature | 0.45MPa,未退火,3.20mm，HDT | ASTM D648 | 86.7 °C |
| Linear coefficient of thermal expansion | MD：-40到40°C | ISO 11359-2 | 5.2E-05 cm/cm/°C |
| Heat distortion temperature | 1.8MPa,未退火,64.0mm跨距，HDT | ISO 75-2/Af | 82.0 °C |
| 1.8MPa,未退火,3.20mm，HDT | ASTM D648 | 82.2 °C |