Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | | 1.13 g/cm³ |
| density | | | 1.21 g/cm³ |
| density | | | 150to180 mPa·s |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Shore hardness | | | 86 |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|
| CriticalExposure | | | 7.60 mJ/cm² |
| Puncture Strength | | | 160.0 µm |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| elongation | Break | ASTM D638 | 5.0to13 % |
| Flexural modulus | | ASTM D790 | 2700to3000 MPa |
| bending strength | | ASTM D790 | 87.0to101 MPa |
| Tensile modulus | | ASTM D638 | 2690to3100 MPa |
| tensile strength | | ASTM D638 | 58.0to68.0 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ASTM D256 | 15to25 J/m |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ASTM D648 | 53.0to55.0 °C |
| Heat distortion temperature | | ASTM D648 | 48.0to50.0 °C |
| Glass Transition Temperature | | DMA | 58.0 °C |
| Linear coefficient of thermal expansion | | ASTME831 | 7.1E-5到1.3E-4 cm/cm/°C |
| Linear coefficient of thermal expansion | | ASTME831 | 1.5E-04 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.