Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
Unspecified 60 3D Systems
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | 3D Systems/ 60 |
|---|---|---|---|
| Impact strength of cantilever beam gap | ASTM D256 | 15to25 J/m |
| hardness | Test Condition | Test Method | 3D Systems/ 60 |
|---|---|---|---|
| Shore hardness | 邵氏D | 86 |
| Supplementary Information | Test Condition | Test Method | 3D Systems/ 60 |
|---|---|---|---|
| Puncture Strength | 160.0 µm | ||
| CriticalExposure | 7.60 mJ/cm² |
| Mechanical properties | Test Condition | Test Method | 3D Systems/ 60 |
|---|---|---|---|
| elongation | 断裂 | ASTM D638 | 5.0to13 % |
| tensile strength | ASTM D638 | 58.0to68.0 MPa | |
| Flexural modulus | ASTM D790 | 2700to3000 MPa | |
| Tensile modulus | ASTM D638 | 2690to3100 MPa | |
| bending strength | ASTM D790 | 87.0to101 MPa |
| physical property | Test Condition | Test Method | 3D Systems/ 60 |
|---|---|---|---|
| density | --2 | 1.13 g/cm³ | |
| --3 | 1.21 g/cm³ | ||
| 粘度(30°C) | 150to180 mPa·s |
| Thermal performance | Test Condition | Test Method | 3D Systems/ 60 |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火，HDT | ASTM D648 | 48.0to50.0 °C |
| 0.45MPa,未退火，HDT | ASTM D648 | 53.0to55.0 °C | |
| Linear coefficient of thermal expansion | MD：0到40°C | ASTME831 | 7.1E-5到1.3E-4 cm/cm/°C |
| MD：75到140°C | ASTME831 | 1.5E-04 cm/cm/°C | |
| Glass Transition Temperature | DMA | 58.0 °C |