Technical Data Sheet
test method | Test Condition | Test Method | Test Result |
---|
Shore hardness | | | 干燥 调节后的 |
Mechanical properties | | | 干燥 调节后的 |
Impact Strength | | | 干燥 调节后的 |
Thermal performance | | | 干燥 调节后的 |
Electrical performance | | | 干燥 调节后的 |
flammability | | | 干燥 调节后的 |
flammability | Test Condition | Test Method | Test Result |
---|
UL flame retardant rating | | UL 94 | V-0 |
Hot filament ignition temperature | | IEC 60695-2-13 | 960 °C |
Limiting Oxygen Index | | ISO 4589-2 | 32 % |
ISO 4589-2 | Test Condition | Test Method | Test Result |
---|
Limiting Oxygen Index | | % | 32 -- |
ISO 179/1eU | Test Condition | Test Method | Test Result |
---|
Impact strength of simply supported beam without notch | | kJ/m² | 60 |
ISO 178 | Test Condition | Test Method | Test Result |
---|
Flexural modulus | | MPa | 7800 5500 |
ISO 1183/A | Test Condition | Test Method | Test Result |
---|
density | | g/cm³ | 1.37 -- |
Mechanical properties | Test Condition | Test Method | Test Result |
---|
tensile strength | | ISO 527-2 | 130 Mpa |
Tensile strain | | ISO 527-2 | 5 % |
Flexural modulus | | ISO 178 | 7800 Mpa |
ISO 527-2 | Test Condition | Test Method | Test Result |
---|
tensile strength | | | 130 MPa |
Tensile strain | | % | 5 |
ISO 868 | Test Condition | Test Method | Test Result |
---|
Shore hardness | | | 90 89 |
IEC 60695-2-13 | Test Condition | Test Method | Test Result |
---|
Hot filament ignition temperature | | °C | 960 -- |
hardness | Test Condition | Test Method | Test Result |
---|
Shore hardness | | ISO 868 | 90 |
UL 94 | Test Condition | Test Method | Test Result |
---|
UL flame retardant rating | | | V-0 -- |
ISO 75-2/Af | Test Condition | Test Method | Test Result |
---|
Heat distortion temperature | | °C | 245 -- |
Impact resistance | Test Condition | Test Method | Test Result |
---|
Impact strength of simply supported beam without notch | | ISO 179/1eU | 60 kJ/m² |
Electrical performance | Test Condition | Test Method | Test Result |
---|
Leakage Traceability Index (Solution A) | | IEC 60112 | 600 V |
Thermal performance | Test Condition | Test Method | Test Result |
---|
Heat distortion temperature | | ISO 75-2/Af | 245 °C |
melting temperature | | ISO 3146 | 260 °C |
ISO 3146 | Test Condition | Test Method | Test Result |
---|
melting temperature | | °C | 260 -- |
IEC 60112 | Test Condition | Test Method | Test Result |
---|
Leakage Traceability Index (Solution A) | | V | 600 -- |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.