PC LNP™ LUBRICOMP™ DZL24 compound
0
CompareTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | ASTM D792 | 1.41 g/cm³ | |
| ASTM D792 | 1.41 g/cm³ | ||
| Shrinkage rate | ASTM D955 | 0.30to0.60 % | |
| ASTM D955 | 0.40to0.70 % | ||
| Water absorption rate | ASTM D570 | 0.12 % | |
| ISO 62 | 0.13 % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| tensile strength | Break | ASTM D638 | 35.0 MPa |
| Break | ISO 527-2/5 | 34.0 MPa | |
| elongation | Yield | ASTM D638 | 5.1 % |
| Tensile strain | Yield | ISO 527-2/5 | 5.1 % |
| elongation | Break | ASTM D638 | 26 % |
| Tensile strain | Break | ISO 527-2/5 | 31 % |
| coefficient of friction | ASTM D3702Modified | 0.45 | |
| ASTM D3702Modified | 0.46 | ||
| Wear factor | ASTM D3702Modified | 4.50 10^-10in^5-min/ft-lb-hr | |
| ASTM D3702Modified | 61.0 10^-10in^5-min/ft-lb-hr | ||
| Flexural modulus | ASTM D790 | 2980 MPa | |
| ISO 178 | 2850 MPa | ||
| bending strength | ISO 178 | 65.0 MPa | |
| ASTM D790 | 70.8 MPa | ||
| Tensile modulus | ASTM D638 | 3200 MPa | |
| ISO 527-2/1 | 2970 MPa | ||
| tensile strength | Yield | ASTM D638 | 37.0 MPa |
| Yield | ISO 527-2/5 | 36.0 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Impact strength of cantilever beam gap | ASTM D256 | 150 J/m | |
| ISO 180/1A | 12 kJ/m² | ||
| ASTM D4812 | 1200 J/m | ||
| Suspended wall beam without notch impact strength | ISO 180/1U | 74 kJ/m² | |
| Dart impact | ASTM D3763 | 24.7 J | |
| Multi axis Instrumented Impact Energy | ISO 6603-2 | 15.2 J |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Linear coefficient of thermal expansion | ASTM D696 | 7.4E-05 cm/cm/°C | |
| Heat distortion temperature | ASTM D648 | 141 °C | |
| ISO 75-2/Bf | 140 °C | ||
| ASTM D648 | 127 °C | ||
| ISO 75-2/Af | 126 °C | ||
| Linear coefficient of thermal expansion | ASTM D696 | 7.3E-05 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.