Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC LNP™ LUBRICOMP™ DZL24 compound SABIC
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC/LNP™ LUBRICOMP™ DZL24 compound |
|---|---|---|---|
| Suspended wall beam without notch impact strength | 23°C | ISO 180/1U | 74 kJ/m² |
| Impact strength of cantilever beam gap | 23°C | ASTM D256 | 150 J/m |
| Dart impact | 23°C,TotalEnergy | ASTM D3763 | 24.7 J |
| Multi axis Instrumented Impact Energy | ISO 6603-2 | 15.2 J | |
| Impact strength of cantilever beam gap | 23°C | ASTM D4812 | 1200 J/m |
| 23°C | ISO 180/1A | 12 kJ/m² |
| Mechanical properties | Test Condition | Test Method | SABIC/LNP™ LUBRICOMP™ DZL24 compound |
|---|---|---|---|
| tensile strength | 屈服 | ISO 527-2/5 | 36.0 MPa |
| elongation | 屈服 | ASTM D638 | 5.1 % |
| Tensile strain | 屈服 | ISO 527-2/5 | 5.1 % |
| Wear factor | Washer | ASTM D3702Modified | 61.0 10^-10in^5-min/ft-lb-hr |
| tensile strength | 屈服 | ASTM D638 | 37.0 MPa |
| Flexural modulus | ISO 178 | 2850 MPa | |
| bending strength | ISO 178 | 65.0 MPa | |
| elongation | 断裂 | ASTM D638 | 26 % |
| tensile strength | 断裂 | ISO 527-2/5 | 34.0 MPa |
| coefficient of friction | Static | ASTM D3702Modified | 0.46 |
| bending strength | 屈服,50.0mm跨距 | ASTM D790 | 70.8 MPa |
| tensile strength | 断裂 | ASTM D638 | 35.0 MPa |
| Tensile modulus | ASTM D638 | 3200 MPa | |
| Tensile strain | 断裂 | ISO 527-2/5 | 31 % |
| Wear factor | Ring | ASTM D3702Modified | 4.50 10^-10in^5-min/ft-lb-hr |
| Flexural modulus | 50.0mm跨距 | ASTM D790 | 2980 MPa |
| coefficient of friction | Dynamic | ASTM D3702Modified | 0.45 |
| Tensile modulus | ISO 527-2/1 | 2970 MPa |
| physical property | Test Condition | Test Method | SABIC/LNP™ LUBRICOMP™ DZL24 compound |
|---|---|---|---|
| Shrinkage rate | MD：24小时 | ASTM D955 | 0.30to0.60 % |
| Water absorption rate | 24hr,50%RH | ASTM D570 | 0.12 % |
| 平衡,23°C,50%RH | ISO 62 | 0.13 % | |
| density | ASTM D792 | 1.41 g/cm³ | |
| Shrinkage rate | TD：24hr | ASTM D955 | 0.40to0.70 % |
| Thermal performance | Test Condition | Test Method | SABIC/LNP™ LUBRICOMP™ DZL24 compound |
|---|---|---|---|
| Heat distortion temperature | 0.45MPa,Unannealed,64.0mmSpan，HDT | ISO 75-2/Bf | 140 °C |
| Linear coefficient of thermal expansion | MD：-30到30°C | ASTM D696 | 7.3E-05 cm/cm/°C |
| TD：-30to30°C | ASTM D696 | 7.4E-05 cm/cm/°C | |
| Heat distortion temperature | 0.45MPa,未退火,3.20mm，HDT | ASTM D648 | 141 °C |
| 1.8MPa,未退火,64.0mm跨距，HDT | ISO 75-2/Af | 126 °C | |
| 1.8MPa,未退火,3.20mm，HDT | ASTM D648 | 127 °C |