Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ISO 1183 | 1.58 g/cm³ |
| Shrinkage rate | | ISO 294-4 | 0.90 % |
| Shrinkage rate | | ISO 294-4 | 0.40 % |
| Water absorption rate | | ISO 62 | 0.50 % |
| Water absorption rate | | ISO 62 | 1.2 % |
| flammability | Test Condition | Test Method | Test Result |
|---|
| Hot filament ignition temperature | | IEC 60695-2-13 | 750 °C |
| Burning wire flammability index | | IEC 60695-2-12 | 675 °C |
| Burning wire flammability index | | IEC 60695-2-12 | 675 °C |
| Burning wire flammability index | | IEC 60695-2-12 | 960 °C |
| Hot filament ignition temperature | | IEC 60695-2-13 | 700 °C |
| Hot filament ignition temperature | | IEC 60695-2-13 | 700 °C |
| UL flame retardant rating | | UL 94 | HB |
| UL flame retardant rating | | UL 94 | HB |
| UL flame retardant rating | | UL 94 | HB |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|
| Automotive Materials | | FMVSS302 | + |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ISO 527-2 | 16800 MPa |
| tensile strength | | ISO 527-2 | 240 MPa |
| Tensile strain | | ISO 527-2 | 2.5 % |
| Flexural modulus | | ISO 178 | 16000 MPa |
| bending strength | | ISO 178 | 350 MPa |
| Poisson's ratio | | ISO 527-2 | 0.40 |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | | ISO 179/1eA | 14 kJ/m² |
| Charpy Notched Impact Strength | | ISO 179/1eA | 15 kJ/m² |
| Impact strength of simply supported beam without notch | | ISO 179/1eU | 91 kJ/m² |
| Impact strength of simply supported beam without notch | | ISO 179/1eU | 95 kJ/m² |
| Impact strength of cantilever beam gap | | ISO 180 | 16 kJ/m² |
| Impact strength of cantilever beam gap | | ISO 180 | 17 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Volume resistivity | | IEC 60093 | 1E+12 ohms·cm |
| dielectric strength | | IEC 60243 | 20 kV/mm |
| arc resistance | | ASTM D495 | PLC 5 |
| Compared to the Leakage Tracking Index (CTI) | | IEC 60112 | PLC 1 |
| High arc combustion index (HAI) | | UL 746 | PLC 0 |
| High arc combustion index (HAI) | | UL 746 | PLC 0 |
| High arc combustion index (HAI) | | UL 746 | PLC 0 |
| High Voltage Arc Traceability Rate (HVTR) | | UL 746 | PLC 1 |
| Hot wire ignition (HWI) | | UL 746 | PLC 4 |
| Hot wire ignition (HWI) | | UL 746 | PLC 3 |
| Hot wire ignition (HWI) | | UL 746 | PLC 4 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Linear coefficient of thermal expansion | | ISO 11359-2 | 1.2E-05 cm/cm/°C |
| Linear coefficient of thermal expansion | | ISO 11359-2 | 1E-04 cm/cm/°C |
| RTI Elec | | UL 746 | 140 °C |
| RTI Elec | | UL 746 | 140 °C |
| RTI Elec | | UL 746 | 140 °C |
| RTI Imp | | UL 746 | 130 °C |
| RTI Imp | | UL 746 | 130 °C |
| RTI Imp | | UL 746 | 130 °C |
| RTI Str | | UL 746 | 140 °C |
| RTI Str | | UL 746 | 140 °C |
| RTI Str | | UL 746 | 140 °C |
| Heat distortion temperature | | ISO 75-2/B | 260 °C |
| Heat distortion temperature | | ISO 75-2/A | 255 °C |
| melting temperature | | ISO 11357-3 | 260 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.