PA66 Vydyne® R550H NT453 Ascend Performance Materials Operations LLC
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

Impact resistanceTest ConditionTest MethodAscend Performance Materials Operations LLC/Vydyne® R550H NT453
Charpy Notched Impact Strength23°CISO 179/1eA15 kJ/m²
-30°CISO 179/1eA14 kJ/m²
Impact strength of cantilever beam gap23°CISO 18017 kJ/m²
Impact strength of simply supported beam without notch23°CISO 179/1eU95 kJ/m²
Impact strength of cantilever beam gap-30°CISO 18016 kJ/m²
Impact strength of simply supported beam without notch-30°CISO 179/1eU91 kJ/m²
Supplementary InformationTest ConditionTest MethodAscend Performance Materials Operations LLC/Vydyne® R550H NT453
Automotive Materialsthicknessd=1mmFMVSS302+
Mechanical propertiesTest ConditionTest MethodAscend Performance Materials Operations LLC/Vydyne® R550H NT453
Flexural modulus23°CISO 17816000 MPa
Tensile strain断裂,23°CISO 527-22.5 %
Tensile modulus23°CISO 527-216800 MPa
tensile strength 断裂,23°CISO 527-2240 MPa
Poisson's ratioISO 527-20.40
bending strength23°CISO 178350 MPa
Electrical performanceTest ConditionTest MethodAscend Performance Materials Operations LLC/Vydyne® R550H NT453
Compared to the Leakage Tracking Index (CTI)3.00mmIEC 60112PLC 1
High Voltage Arc Traceability Rate (HVTR)HVTRUL 746PLC 1
dielectric strength1.00mmIEC 6024320 kV/mm
arc resistance3.00mmASTM D495PLC 5
Hot wire ignition (HWI)0.75mmUL 746PLC 4
1.5mmUL 746PLC 3
High arc combustion index (HAI)1.5mmUL 746PLC 0
Volume resistivity0.750mmIEC 600931E+12 ohms·cm
Hot wire ignition (HWI)3.0mmUL 746PLC 4
High arc combustion index (HAI)3.0mmUL 746PLC 0
0.75mmUL 746PLC 0
flammabilityTest ConditionTest MethodAscend Performance Materials Operations LLC/Vydyne® R550H NT453
Burning wire flammability index3.0mmIEC 60695-2-12960 °C
UL flame retardant rating0.75mmUL 94HB
3.0mmUL 94HB
Hot filament ignition temperature3.0mmIEC 60695-2-13750 °C
Burning wire flammability index1.5mmIEC 60695-2-12675 °C
Hot filament ignition temperature1.5mmIEC 60695-2-13700 °C
Burning wire flammability index0.75mmIEC 60695-2-12675 °C
UL flame retardant rating1.5mmUL 94HB
Hot filament ignition temperature0.75mmIEC 60695-2-13700 °C
physical property Test ConditionTest MethodAscend Performance Materials Operations LLC/Vydyne® R550H NT453
Shrinkage rateMD:23°C,2.00mmISO 294-40.40 %
Water absorption rate23°C,24hrISO 620.50 %
平衡,23°C,50%RHISO 621.2 %
densityISO 11831.58 g/cm³
Shrinkage rateTD:23°C,2.00mmISO 294-40.90 %
Thermal performanceTest ConditionTest MethodAscend Performance Materials Operations LLC/Vydyne® R550H NT453
RTI Str0.75mmUL 746140 °C
RTI Imp1.5mmUL 746130 °C
RTI Elec3.0mmUL 746140 °C
RTI Imp3.0mmUL 746130 °C
RTI Elec0.75mmUL 746140 °C
RTI Imp0.75mmUL 746130 °C
melting temperatureISO 11357-3260 °C
Linear coefficient of thermal expansionTD：23to55°C,2.00mmISO 11359-21E-04 cm/cm/°C
Heat distortion temperature0.45MPa,未退火，HDTISO 75-2/B260 °C
RTI Str1.5mmUL 746140 °C
Heat distortion temperature1.8MPa,未退火，HDTISO 75-2/A255 °C
RTI Str3.0mmUL 746140 °C
Linear coefficient of thermal expansionMD：23to55°C,2.00mmISO 11359-21.2E-05 cm/cm/°C
RTI Elec1.5mmUL 746140 °C