TSU-Ester InnoTuf® HP-1060A Innovative Polymers, Inc.
0
CompareTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | 1.16 g/cm³ | ||
| 1.18 g/cm³ | |||
| Base Resin | 1.20 g/cm³ | ||
| Shrinkage rate | ASTM D2566 | 1.0to1.5 % |
| thermosetting | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Thermosetting components | Hardener | 按重量计算的混合比:100按容量计算的混合比:100 | |
| 1300to1400 min | |||
| Resin | 按重量计算的混合比:43按容量计算的混合比:42 |
| Uncured Properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Viscosity | 0.70 Pa·s | ||
| 0.72 Pa·s | |||
| 0.73 Pa·s | |||
| 1.8E+02 hr | |||
| 5.0to15 min |
| Cured Properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| tear strength | ASTM D624 | 22.8 kN/m | |
| Shore hardness | ASTM D2240 | 55to65 | |
| tensile strength | ASTM D638 | 5.86 MPa | |
| elongation | Break | ASTM D638 | 800 % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Taber abraser | ASTM D4060 | 4.00 mg |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.