Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
TSU-Ester InnoTuf® HP-1060A Innovative Polymers, Inc.
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Mechanical properties | Test Condition | Test Method | Innovative Polymers, Inc./InnoTuf® HP-1060A |
|---|---|---|---|
| Taber abraser | 1000Cycles,1000g,H-18转轮 | ASTM D4060 | 4.00 mg |
| thermosetting | Test Condition | Test Method | Innovative Polymers, Inc./InnoTuf® HP-1060A |
|---|---|---|---|
| Thermosetting components | 硬化法 | 按重量计算的混合比:100按容量计算的混合比:100 | |
| 树脂 | 按重量计算的混合比:43按容量计算的混合比:42 | ||
| 脱模时间(66°C) | 1300to1400 min |
| Uncured Properties | Test Condition | Test Method | Innovative Polymers, Inc./InnoTuf® HP-1060A |
|---|---|---|---|
| Viscosity | 固化时间5 | 1.8E+02 hr | |
| 60°C3 | 0.72 Pa·s | ||
| 60°C4 | 0.73 Pa·s | ||
| GelTime | 5.0to15 min | ||
| 60°C2 | 0.70 Pa·s |
| Cured Properties | Test Condition | Test Method | Innovative Polymers, Inc./InnoTuf® HP-1060A |
|---|---|---|---|
| tear strength | ASTM D624 | 22.8 kN/m | |
| elongation | 断裂 | ASTM D638 | 800 % |
| tensile strength | ASTM D638 | 5.86 MPa | |
| Shore hardness | ShoreA | ASTM D2240 | 55to65 |
| physical property | Test Condition | Test Method | Innovative Polymers, Inc./InnoTuf® HP-1060A |
|---|---|---|---|
| density | Hardener | 1.16 g/cm³ | |
| 基体树脂 | 1.20 g/cm³ | ||
| Cured | 1.18 g/cm³ | ||
| Shrinkage rate | MD | ASTM D2566 | 1.0to1.5 % |