Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ISO 1183 | 1.06 g/cm³ |
| Melt volume flow rate | | ISO 1133 | 17.0 cm³/10min |
| Shrinkage rate | | | 0.50to0.70 % |
| Shrinkage rate | | | 0.50to0.70 % |
| Water absorption rate | | ISO 62 | 0.070 % |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | HB |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of simply supported beam without notch | | ISO 179 | 150 kJ/m² |
| Charpy Notched Impact Strength | | ISO 179 | 17 kJ/m² |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ISO 527-2 | 2500 MPa |
| tensile strength | | ISO 527-2 | 43.0 MPa |
| Tensile strain | | ISO 527-2 | 3.2 % |
| Nominal tensile fracture strain | | ISO 527-2 | 34 % |
| bending strength | | ISO 178 | 76.0 MPa |
| Flexural modulus | | ISO 178 | 2500 MPa |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| dielectric strength | | IEC 60243-1 | 20 kV/mm |
| dielectric strength | | IEC 60243-1 | 38 kV/mm |
| Volume resistivity | | IEC 60093 | 3E+16 ohms·cm |
| Surface Resistivity | | IEC 60093 | 2E+15 ohms |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ISO 75-2/B | 110 °C |
| Linear coefficient of thermal expansion | | ISO 11359-2 | 7.1E-05 cm/cm/°C |
| Linear coefficient of thermal expansion | | ISO 11359-2 | 6.7E-05 cm/cm/°C |
| Heat distortion temperature | | ISO 75-2/A | 95.0 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.
Compare