PPO(PPE)+PS Iupiace® AH40 Mitsubishi Chemical Corporation
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

Impact resistanceTest ConditionTest MethodMitsubishi Chemical Corporation/Iupiace® AH40
Charpy Notched Impact Strength23°CISO 17917 kJ/m²
Impact strength of simply supported beam without notch23°CISO 179150 kJ/m²
Electrical performanceTest ConditionTest MethodMitsubishi Chemical Corporation/Iupiace® AH40
dielectric strength3.00mmIEC 60243-120 kV/mm
Volume resistivityIEC 600933E+16 ohms·cm
dielectric strength1.00mmIEC 60243-138 kV/mm
Surface ResistivityIEC 600932E+15 ohms
Mechanical propertiesTest ConditionTest MethodMitsubishi Chemical Corporation/Iupiace® AH40
Flexural modulus23°CISO 1782500 MPa
Tensile modulus23°CISO 527-22500 MPa
tensile strength 屈服,23°CISO 527-243.0 MPa
Tensile strain屈服,23°CISO 527-23.2 %
Nominal tensile fracture strain23°CISO 527-234 %
bending strength23°CISO 17876.0 MPa
flammabilityTest ConditionTest MethodMitsubishi Chemical Corporation/Iupiace® AH40
UL flame retardant rating0.75mmUL 94HB
physical property Test ConditionTest MethodMitsubishi Chemical Corporation/Iupiace® AH40
Shrinkage rateTD:3.20mm0.50to0.70 %
MD:3.20mm0.50to0.70 %
Water absorption rate饱和,23°CISO 620.070 %
densityISO 11831.06 g/cm³
Melt volume flow rate300°C/2.16kgISO 113317.0 cm³/10min
Thermal performanceTest ConditionTest MethodMitsubishi Chemical Corporation/Iupiace® AH40
Heat distortion temperature0.45MPa,未退火,HDTISO 75-2/B110 °C
1.8MPa,未退火,HDTISO 75-2/A95.0 °C
Linear coefficient of thermal expansionMDISO 11359-26.7E-05 cm/cm/°C
TDISO 11359-27.1E-05 cm/cm/°C