Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ISO 1183 | 1.20 g/cm³ |
| Melt volume flow rate | | ISO 1133 | 15.0 cm³/10min |
| Shrinkage rate | | ASTM D955 | 0.50to0.70 % |
| Shrinkage rate | | ASTM D955 | 0.50to0.70 % |
| Water absorption rate | | ISO 62 | 0.20 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | R-Scale | ASTM D785 | 118 |
| optical performance | Test Condition | Test Method | Test Result |
|---|
| refractive index | | ASTM D542 | 1.585 |
| transmissivity | | ASTM D1003 | 89.0 % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| elongation | Break | ISO 527-2 | 110 % |
| Flexural modulus | | ASTM D790 | 2200 MPa |
| Flexural modulus | | ISO 178 | 2300 MPa |
| bending strength | | ASTM D790 | 89.0 MPa |
| bending strength | | ISO 178 | 85.0 MPa |
| Tensile modulus | | ISO 527-2 | 2300 MPa |
| tensile strength | | ASTM D638 | 62.0 MPa |
| tensile strength | | ISO 527-2 | 60.0 MPa |
| elongation | Break | ASTM D638 | 130 % |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | | ISO 179 | 70 kJ/m² |
| Impact strength of cantilever beam gap | | ASTM D256 | 840 J/m |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Surface Resistivity | | IEC 60093 | >1.0E+15 ohms |
| Volume resistivity | | IEC 60093 | 3E+16 ohms·cm |
| dielectric strength | | ASTM D149 | 20 kV/mm |
| arc resistance | | ASTM D495 | 110 sec |
| Compared to the Leakage Tracking Index (CTI) | | IEC 60112 | PLC 2 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ASTM D648 | 140 °C |
| Heat distortion temperature | | ASTM D648 | 134 °C |
| Linear coefficient of thermal expansion | | ASTM D696 | 7E-05 cm/cm/°C |
| Heat distortion temperature | | ISO 75-2/A | 126 °C |
| Linear coefficient of thermal expansion | | ASTM D696 | 7E-05 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.