Technical Data Sheet
physical property | Test Condition | Test Method | Test Result |
---|
melt mass-flow rate | | ASTM D1238 | 6.0 g/10min |
Shrinkage rate | | | 1.7 % |
processability | Test Condition | Test Method | Test Result |
---|
Dry conditions | | | 热风干燥 80℃---约3-4小时 |
process temperature | | | 170 °C |
process temperature | | | 190 °C |
process temperature | | | 180 °C |
process temperature | | | 180-210 °C |
screw speed | | | 80-120 rpm |
Temperature | | | ≦40 °C |
Mechanical properties | Test Condition | Test Method | Test Result |
---|
Tensile modulus | | ASTM D638/ISO 527 | 1600 kg/cm²(MPa)[Lb/in²] |
Flexural modulus | | ASTM D790/ISO 178 | 1400 kg/cm²(MPa)[Lb/in²] |
bending strength | | ASTM D790/ISO 178 | 48 kg/cm²(MPa)[Lb/in²] |
elongation at break | | ASTM D638/ISO 527 | >100 % |
tensile strength | | ASTM D638 | 34.3 Mpa |
Stretching length | | ASTM D638 | >300 % |
bending strength | | ASTM D790 | 44.1 Mpa |
Flexural modulus | | ASTM D790 | 1.38 GPa |
Impact strength of cantilever beam gap | | ASTM D256 | 180 J/m |
Rockwell hardness | | ASTM D785 | 75 M |
Physical properties | Test Condition | Test Method | Test Result |
---|
density | | ASTM D792/ISO 1183 | 1.35 |
Shrinkage rate | | ASTM D955 | 1.7 % |
Electrical performance | Test Condition | Test Method | Test Result |
---|
Surface Resistivity | | ASTM D257 | 1×10 |
Volume resistivity | | ASTM D257 | 1×10 |
Thermal performance | Test Condition | Test Method | Test Result |
---|
Combustibility (rate) | | UL 94 | HB |
Linear coefficient of thermal expansion | | ASTM D696/ISO 11359 | 1.2E-04 mm/mm.℃ |
UL flame retardant rating | | UL 94 | HB |
Heat distortion temperature | | ASTM D648 | 147 °C |
Heat distortion temperature | | ASTM D648 | 94 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.