Material Comparison

Product Info
Product Name
Brand Name
Usages
Properties
Certificates
POM FU2025 MITSUBISHI ENGINEERING JAPAN
Iupital™ 
Automotive sector、Electronic and Electrical
wear resistant、High mobility
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

Mechanical propertiesTest ConditionTest MethodMITSUBISHI ENGINEERING JAPAN/FU2025
bending strengthASTM D790/ISO 17848 kg/cm²(MPa)[Lb/in²]
Impact strength of cantilever beam gap3.2mmASTM D256180 J/m
Flexural modulusASTM D790/ISO 1781400 kg/cm²(MPa)[Lb/in²]
Rockwell hardnessASTM D78575 M
tensile strength 23℃ASTM D63834.3 Mpa
Tensile modulusASTM D638/ISO 5271600 kg/cm²(MPa)[Lb/in²]
elongation at breakASTM D638/ISO 527>100 %
bending strength23℃ASTM D79044.1 Mpa
Flexural modulus23℃ASTM D7901.38 GPa
Stretching length23℃ASTM D638＞300 %
Electrical performanceTest ConditionTest MethodMITSUBISHI ENGINEERING JAPAN/FU2025
Surface ResistivityASTM D2571×10
Volume resistivityASTM D2571×10
Physical propertiesTest ConditionTest MethodMITSUBISHI ENGINEERING JAPAN/FU2025
Shrinkage rateASTM D9551.7 %
densityASTM D792/ISO 11831.35
processabilityTest ConditionTest MethodMITSUBISHI ENGINEERING JAPAN/FU2025
process temperature180-210 °C
Dry conditions热风干燥 80℃---约3-4小时
screw speed80-120 rpm
Temperature≦40 °C
physical property Test ConditionTest MethodMITSUBISHI ENGINEERING JAPAN/FU2025
Shrinkage rate平行方向1.7 %
melt mass-flow rateASTM D12386.0 g/10min
Thermal performanceTest ConditionTest MethodMITSUBISHI ENGINEERING JAPAN/FU2025
Combustibility (rate)UL 94HB
Heat distortion temperature455Kpa，HDTASTM D648147 °C
820Kpa，HDTASTM D64894 °C
Linear coefficient of thermal expansionASTM D696/ISO 113591.2E-04 mm/mm.℃
UL flame retardant ratingUL 94HB