Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Shrinkage rate of wire forming | | ISO 294 | 0.90 % |
| Shrinkage rate of wire forming | | ISO 294 | 0.85 % |
| Basic performance | Test Condition | Test Method | Test Result |
|---|
| density | | ISO 1183 | 1.16 g/cm |
| Water absorption | | ISO 62 | 8.0 % |
| | ISO 62 | 0.85 % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| tensile yield strength | | ISO 527 | 90(45) Mpa |
| Impact Strength | | ISO 179/1eU | >100(>100) KJ/m |
| elongation at break | | ISO 527 | 3(15) % |
| Impact Strength | | ISO 179/1eA | 3(15) KJ/m |
| Tensile modulus | | ISO 527 | 3700(1200) Mpa |
| elongation at break | | ISO 527 | 4(>50) % |
| tensile breaking strength | | ISO 527 | 70(-) Mpa |
| Other performance | Test Condition | Test Method | Test Result |
|---|
| oxygen index | | ISO 4589-2 | >32 % |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Volume resistivity | | IEC 60093 | 10 Ω.cm |
| dielectric constant | | IEC 60250 | 3.0(8.0) |
| Surface Resistivity | | IEC 60093 | 10 Ω |
| arc resistance | | IEC 60112 | 575 |
| Dielectric loss factor | | IEC 60250 | 200(850) |
| dielectric constant | | IEC 60250 | 4.0(4.0) |
| dielectric strength | | IEC 60243-1 | 32(29) KV/mm |
| Dielectric loss factor | | IEC 60250 | 30(1000) |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heating wire temperature | | ISO 11359-2 | 960 °C |
| | ISO 11359 | 0.9 |
| | ISO 11359 | 0.7 |
| | ISO 75 | 185 °C |
| | ISO 75 | 65 °C |
| melting point | | ISO 11357 | 222 °C |
| Flame retardancy | | ISO 1210 | V-0 rating |
| Maximum operating temperature | | ISO 2578 | 100-120 °C |
| Maximum operating temperature | | ISO 2578 | 180 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.