Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Shrinkage rate | | ISO294-4 | 0.80 % |
| Shrinkage rate | | ISO294-4 | 0.30 % |
| Water absorption rate | | ISO62 | <0.020 % |
| processability | Test Condition | Test Method | Test Result |
|---|
| Shrinkage rate | | ASTM D-955 | 0.3 % |
| Shrinkage rate | | ASTM D-955 | 0.7 % |
| Dry conditions | | | 120~150度 2.0～5.0hr |
| process temperature | | | 270~300 °C |
| process temperature | | | 290~330 °C |
| screw speed | | | 100~150 rpm |
| Temperature | | | 135~150 °C |
| pressure | | | 1.00~20.0 Mpa |
| other | Test Condition | Test Method | Test Result |
|---|
| | | 韧性良好 |
| colour | | | 黑色 |
| purpose | | | 注射型 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL94 | V-0 |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|
| BarFlowLength | | 内部方法 | 175 mm |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| | ASTM D-638 | 1.7 % |
| tensile strength | | ASTM D-638 | 172 Mpa |
| Charpy impact strength | | ASTM D-256 | 74 J/m |
| Charpy impact strength | | ASTM D-256 | 541 J/m |
| Rockwell hardness | | ASTM D-785 | 122 |
| bending strength | | ASTM D-790 | 275 Mpa |
| Flexural modulus | | ASTM D-790 | 15 GPa |
| Tensile stress | | ISO527-2 | 176 Mpa |
| Tensile strain | | ISO527-2 | 1.5 % |
| Flexural modulus | | ISO178 | 14700 Mpa |
| Bending stress | | ISO178 | 275 Mpa |
| Tensile Weld Strength | | 内部方法 | 60.0 Mpa |
| Izod notch impact strength | | ASTM D256/ISO 179 | 82 kg·cm/cm(J/M)ft·lb/in |
| elongation at break | | ASTM D638/ISO 527 | 1.5 % |
| tensile strength | | ASTM D638/ISO 527 | 176 kg/cm²(MPa)[Lb/in²] |
| Flexural modulus | | ASTM D790/ISO 178 | 14700 kg/cm²(MPa)[Lb/in²] |
| bending strength | | ASTM D790/ISO 178 | 275 kg/cm²(MPa)[Lb/in²] |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Volume resistance value | | ASTM D-257 | 4×1016 Ω.cm |
| dielectric constant | | ASTM D-150 | 3.9 |
| Dissipation coefficient | | ASTM D-150 | 0.0014 |
| Dielectric breakdown strength | | ASTM D-149 | 16 KV/mm |
| Thermal conductivity | | 自定标准 | 0.27 W/m.K |
| Volume resistivity | | IEC60093 | 1E+17 ohms·cm |
| dielectric strength | | IEC60243-1 | 16 KV/mm |
| dielectric constant | | IEC60250 | 3.90 |
| Dissipation Factor | | IEC60250 | 1.4E-03 |
| Compared to the Leakage Tracking Index (CTI) | | UL746 | PLC 4 |
| CTI | | IEC60112 | 125 V |
| dielectric constant | | ASTM D150/IEC 60250 | 3.90 |
| Physical properties | Test Condition | Test Method | Test Result |
|---|
| density | | ASTM D792/ISO 1183 | 1.64 |
| Mold Shrinkage | | ASTM D955 | 0.3~0.8 % |
| Water absorption rate | | ASTM D570/ISO 62 | 0.02 % |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| | 自定标准 | 2.2 |
| Flame retardancy | | UL 94 | V-0 |
| | ASTM D-648 | ＞260 °C |
| | ISO75-2/A | >260 °C |
| melting temperature | | 内部方法 | 285 °C |
| | ASTM D648/ISO 75 | 260 ℃（℉） |
| melting point | | | 285 ℃（℉） |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.