Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PPS GS-40 TOSOH JAPAN
SUSTEEL®
Fiber grade
enhance、Glass fiber reinforced
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Supplementary Information | Test Condition | Test Method | TOSOH JAPAN/GS-40 |
|---|---|---|---|
| BarFlowLength | 内部方法 | 175 mm |
| Mechanical properties | Test Condition | Test Method | TOSOH JAPAN/GS-40 |
|---|---|---|---|
| Impact strength of cantilever beam gap | ASTM D256/ISO 179 | 82 kg·cm/cm(J/M)ft·lb/in | |
| bending strength | ASTM D790/ISO 178 | 275 kg/cm²(MPa)[Lb/in²] | |
| Flexural modulus | ASTM D790/ISO 178 | 14700 kg/cm²(MPa)[Lb/in²] | |
| bending strength | ASTM D-790 | 275 Mpa | |
| tensile strength | ASTM D-638 | 172 Mpa | |
| elongation at break | ASTM D638/ISO 527 | 1.5 % | |
| Flexural modulus | ASTM D-790 | 15 GPa | |
| tensile strength | ASTM D638/ISO 527 | 176 kg/cm²(MPa)[Lb/in²] | |
| Charpy Notched Impact Strength | 有缺口 | ASTM D-256 | 74 J/m |
| bending strength | ISO 178 | 275 Mpa | |
| Tensile strain | 断裂 | ISO 527-2 | 1.5 % |
| Flexural modulus | ISO 178 | 14700 Mpa | |
| Tensile Weld Strength | 内部方法 | 60.0 Mpa | |
| Charpy Notched Impact Strength | 无缺口 | ASTM D-256 | 541 J/m |
| tensile strength | 屈服 | ISO 527-2 | 176 Mpa |
| Rockwell hardness | ASTM D-785 | 122 | |
| elongation at break | ASTM D-638 | 1.7 % |
| Electrical performance | Test Condition | Test Method | TOSOH JAPAN/GS-40 |
|---|---|---|---|
| Dissipation Factor | 1MHz | ASTM D-150 | 0.0014 |
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | PLC 4 | |
| thermal conductivity | 自定标准 | 0.27 W/m.K | |
| Volume resistivity | ASTM D-257 | 4×1016 Ω.cm | |
| dielectric strength | IEC 60243-1 | 16 KV/mm | |
| dielectric constant | 1MHz | ASTM D-150 | 3.9 |
| Volume resistivity | IEC 60093 | 1E+17 ohms·cm | |
| dielectric strength | ASTM D-149 | 16 KV/mm | |
| dielectric constant | ASTM D150/IEC 60250 | 3.90 | |
| 1MHz | IEC 60250 | 3.90 | |
| Compared to the Leakage Tracking Index (CTI) | CTI | UL 746 | PLC 4 |
| Dissipation Factor | 1MHz | IEC 60250 | 1.4E-03 |
| other | Test Condition | Test Method | TOSOH JAPAN/GS-40 |
|---|---|---|---|
| characteristic | 韧性良好 | ||
| Color | 黑色 | ||
| purpose | 注射型 |
| Physical properties | Test Condition | Test Method | TOSOH JAPAN/GS-40 |
|---|---|---|---|
| Shrinkage rate | ASTM D955 | 0.3-0.8 % | |
| density | ASTM D792/ISO 1183 | 1.64 | |
| Water absorption rate | ASTM D570/ISO 62 | 0.02 % |
| processability | Test Condition | Test Method | TOSOH JAPAN/GS-40 |
|---|---|---|---|
| process temperature | 290-330 °C | ||
| pressure | 1.00-20.0 Mpa | ||
| Shrinkage rate | 垂直方向 | ASTM D-955 | 0.7 % |
| 流动方向 | ASTM D-955 | 0.3 % | |
| Dry conditions | 120-150度 2.0-5.0hr | ||
| screw speed | 100-150 rpm | ||
| Temperature | 135-150 °C |
| flammability | Test Condition | Test Method | TOSOH JAPAN/GS-40 |
|---|---|---|---|
| UL flame retardant rating | UL 94 | V-0 |
| physical property | Test Condition | Test Method | TOSOH JAPAN/GS-40 |
|---|---|---|---|
| Shrinkage rate | TD | ISO 294-4 | 0.80 % |
| MD | ISO 294-4 | 0.30 % | |
| Water absorption rate | 平衡,23°C,50%RH | ISO 62 | <0.020 % |
| Thermal performance | Test Condition | Test Method | TOSOH JAPAN/GS-40 |
|---|---|---|---|
| melting temperature | 内部方法 | 285 °C | |
| Heat distortion temperature | 1.82MPa，HDT | ASTM D-648 | ＞260 °C |
| HDT | ASTM D648/ISO 75 | 260 ℃（℉） | |
| Linear coefficient of thermal expansion | 自定标准 | 2.2 | |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | >260 °C |
| melting temperature | 285 ℃（℉） | ||
| UL flame retardant rating | UL 94 | V-0 |