| physical property | Test Condition | Test Method | Test Result |
|---|
| viscosity number | | ISO 307 | 196 cm³/g |
| optical performance | Test Condition | Test Method | Test Result |
|---|
| Clarity | | 内部方法 | 83 % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| | ISO 8295 | 1.0 |
| | ISO 8295 | 1.2 |
| Filling analysis | Test Condition | Test Method | Test Result |
|---|
| melt viscosity | | 内部方法 | 810000 mPa·s |
| Average Specific Heat Capacity | | | 2250 J/kg/°C |
| Puncture Resistance | | 内部方法 | 13.0 J/cm |
| RSV - Formic Acid, 1g/100ml | | 内部方法 | 3.03 |
| squeeze out | Test Condition | Test Method | Test Result |
|---|
| | | 270 °C |
| | | 270 °C |
| Temperature in Zone 3 of the material cylinder | | | 270 °C |
| | | 270 °C |
| die temperature | | | 270 °C |
| pull roll | | | 110 °C |
| film | Test Condition | Test Method | Test Result |
|---|
| Film thickness - tested | | | 50 µm |
| Tensile modulus 2 | | 内部方法 | 455 Mpa |
| | ISO 527-3 | 31.0 Mpa |
| | ISO 527-3 | 82.0 Mpa |
| Elongation - MD | | ISO 527-3 | 350 % |
| Trouser Tear - Parallel | | ISO 6383-1 | 32.0 |
| Water vapor permeability | | DIS 15106-1/-3 | 35 g/m²/24 hr |
| Oxygen transmission rate | | ASTM D256A | 26 cm³/m²/bar/24 hr |
| Oxygen transmission rate | | ASTM D256A | 38 cm³/m²/bar/24 hr |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| | ISO 11359-2 | 9.0E-5 cm/cm/°C |
| Specific Heat Capacity | | | 1550 J/kg/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.