PA66

PA66 Amilan® CM3001G33 TORAY SHENZHEN

Properties:
Medium viscosity
Usages:
Electrical fieldElectronic fieldAutomotive sector
Certificates:
MSDS
Compare View Prices

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Charpy Notched Impact Strength	-40°C	ISO 179	10 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	23°C	ISO 179	13 kJ/m²
Impact strength of simply supported beam without notch	23°C	ISO 179	65 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	-40°C	ISO 179	60 kJ/m²

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	0.79 mm	UL 94	HB

mechanical properties	Test Condition	Test Method	Test Result
tensile strength	-40°C	ISO 527-2	235 Mpa
	tensile strength	23°C	ISO 527-2	190 Mpa
	tensile strength	tensile strength	80°C	ISO 527-2	120 Mpa
Tensile strain	Break, -40°C	ISO 527-2	2.0 %
	Tensile strain	Break, 23°C	ISO 527-2	2.5 %
	Tensile strain	Tensile strain	Break, 80°C	ISO 527-2	5.0 %
Bending modulus	-40°C	ISO 178	11600 Mpa
	Bending modulus	23°C	ISO 178	9500 Mpa
	Bending modulus	Bending modulus	80°C	ISO 178	5800 Mpa
bending strength	-40°C	ISO 178	325 Mpa
	bending strength	23°C	ISO 178	290 Mpa
	bending strength	bending strength	80°C	ISO 178	190 Mpa
Compressive stress	-40°C	ISO 604	250 Mpa
	Compressive stress	23°C	ISO 604	180 Mpa
	Compressive stress	Compressive stress	80°C	ISO 604	110 Mpa
shear strength	23°C	ASTM D732	95.0 Mpa
Taber abraser	1000 Cycles	ISO 9352	0.400 mg
Friction coefficient - vs. Metal		Suzuki Method	0.15

thermal performance	Test Condition	Test Method	Test Result
thermal conductivity			0.40 W/m/K
specific heat			1800 J/kg/°C
Linear coefficient of thermal expansion	Flow	ISO 11359-2	2.0E-5 - 3.0E-5 cm/cm/°C
Melting temperature		DSC	265 °C
Hot deformation temperature	0.45 MPa, Unannealed	ISO 75-2/B	262 °C

Physical properties	Test Condition	Test Method	Test Result
density	23°C	ISO 1183	1.37 g/cm³
Shrinkage rate	横向Flow : 3.00 mm	Internal Method	0.60 - 0.90 %
Shrinkage rate	Shrinkage rate	Flow : 3.00 mm	Internal Method	0.20 - 0.50 %
Water absorption rate	24 hr, 23°C	ISO 62	0.60 %
Water absorption rate	Water absorption rate	Saturation, 23°C	ISO 62	5.5 %

Electrical performance	Test Condition	Test Method	Test Result
Arc resistance		UL 746	114 sec
Dissipation factor	23°C, 1 MHz	IEC 60250	0.020
	Dissipation factor	23°C, 1 kHz	IEC 60250	0.020
	Dissipation factor	Dissipation factor	23°C, 50 Hz	IEC 60250	0.020
Dielectric constant	23°C, 1 MHz	IEC 60250	3.90
	Dielectric constant	23°C, 1 kHz	IEC 60250	4.40
	Dielectric constant	Dielectric constant	23°C, 50 Hz	IEC 60250	4.60
Dielectric strength		IEC 60243-1	20 KV/mm
Volume resistivity		IEC 60093	1.0E+13 ohms·cm

hardness	Test Condition	Test Method	Test Result
Rockwell hardness	M -Sale, 23°C	ISO 2039-2	97
	Rockwell hardness	R -Sale, 80°C	ISO 2039-2	24
	Rockwell hardness	Rockwell hardness	R -Sale, 23°C	ISO 2039-2	121

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

PA66 Amilan® CM3001G33 TORAY SHENZHEN

Technical Data Sheet