Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA66 CM3001G33 TORAY SHENZHEN
Amilan®
Electrical field、Electronic field、Automotive sector
Medium viscosity
MSDS
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | TORAY SHENZHEN/CM3001G33 |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179 | 13 kJ/m² |
| -40°C | ISO 179 | 10 kJ/m² | |
| Impact strength of simply supported beam without notch | -40°C | ISO 179 | 60 kJ/m² |
| 23°C | ISO 179 | 65 kJ/m² |
| hardness | Test Condition | Test Method | TORAY SHENZHEN/CM3001G33 |
|---|---|---|---|
| Rockwell hardness | M 计秤, 23°C | ISO 2039-2 | 97 |
| R 计秤, 23°C | ISO 2039-2 | 121 | |
| R 计秤, 80°C | ISO 2039-2 | 24 |
| Mechanical properties | Test Condition | Test Method | TORAY SHENZHEN/CM3001G33 |
|---|---|---|---|
| Tensile strain | 断裂, 80°C | ISO 527-2 | 5.0 % |
| Bending stress | 23°C | ISO 178 | 290 Mpa |
| compression stress | -40°C | ISO 604 | 250 Mpa |
| Taber Abrasion Resistance | 1000 Cycles | ISO 9352 | 0.400 mg |
| Friction coefficient - vs. Metal 4 | Suzuki Method | 0.15 | |
| Tensile stress | -40°C | ISO 527-2 | 235 Mpa |
| compression stress | 23°C | ISO 604 | 180 Mpa |
| 80°C | ISO 604 | 110 Mpa | |
| Flexural modulus | 80°C | ISO 178 | 5800 Mpa |
| Bending stress | -40°C | ISO 178 | 325 Mpa |
| 80°C | ISO 178 | 190 Mpa | |
| Tensile strain | 断裂, -40°C | ISO 527-2 | 2.0 % |
| 断裂, 23°C | ISO 527-2 | 2.5 % | |
| shear strength | 23°C | ASTM D732 | 95.0 Mpa |
| Flexural modulus | -40°C | ISO 178 | 11600 Mpa |
| 23°C | ISO 178 | 9500 Mpa | |
| Tensile stress | 80°C | ISO 527-2 | 120 Mpa |
| 23°C | ISO 527-2 | 190 Mpa |
| Electrical performance | Test Condition | Test Method | TORAY SHENZHEN/CM3001G33 |
|---|---|---|---|
| Dissipation Factor | 23°C, 1 kHz | IEC 60250 | 0.020 |
| dielectric constant | 23°C, 50 Hz | IEC 60250 | 4.60 |
| dielectric strength | IEC 60243-1 | 20 KV/mm | |
| Volume resistivity | IEC 60093 | 1.0E+13 ohms·cm | |
| Dissipation Factor | 23°C, 1 MHz | IEC 60250 | 0.020 |
| dielectric constant | 23°C, 1 MHz | IEC 60250 | 3.90 |
| Arc Resistance | UL 746 | 114 sec | |
| dielectric constant | 23°C, 1 kHz | IEC 60250 | 4.40 |
| Dissipation Factor | 23°C, 50 Hz | IEC 60250 | 0.020 |
| flammability | Test Condition | Test Method | TORAY SHENZHEN/CM3001G33 |
|---|---|---|---|
| UL flame retardant rating | 0.79 mm | UL 94 | HB |
| physical property | Test Condition | Test Method | TORAY SHENZHEN/CM3001G33 |
|---|---|---|---|
| density | 23°C | ISO 1183 | 1.37 g/cm³ |
| Shrinkage rate 3 | 横向流量 : 3.00 mm | 内部方法 | 0.60 到 0.90 % |
| 流量 : 3.00 mm | 内部方法 | 0.20 到 0.50 % | |
| Water absorption rate | 24 hr, 23°C | ISO 62 | 0.60 % |
| 饱和, 23°C | ISO 62 | 5.5 % |
| Thermal performance | Test Condition | Test Method | TORAY SHENZHEN/CM3001G33 |
|---|---|---|---|
| thermal conductivity | 0.40 W/m/K | ||
| Heat Deflection Temperature | 0.45 MPa, 未退火 | ISO 75-2/B | 262 °C |
| Coefficient of Linear Thermal Expansion (Flow) | ISO 11359-2 | 2.0E-5 到 3.0E-5 cm/cm/°C | |
| melting temperature | DSC | 265 °C | |
| specific heat | 1800 J/kg/°C |