Product Name / Manufacturer / Model

Grade

Reference Price

PEI SABIC INNOVATIVE US 1010M-1100

Injection grade

US$ 14,190 / MT

FOB Guangzhou port, China

mechanical properties	Test Condition	Test Method	SABIC INNOVATIVE US/1010M-1100
bending strength		ISO 178	160 Mpa
Bending modulus		ISO 178	3300 Mpa
Tensile strain	Yield	ISO 527-2/50	6.0 %
Tensile modulus		ISO 527-2/1	3200 Mpa
Taber abraser	1000 Cycles, 1000 g, CS-17 Wheel	Internal Method	10.0 mg
tensile strength	Break	ISO 527-2/50	85.0 Mpa
tensile strength		Yield	ISO 527-2/50	105 Mpa
Tensile strain	Break	ISO 527-2/50	60 %
thermal performance	Test Condition	Test Method	SABIC INNOVATIVE US/1010M-1100
Linear coefficient of thermal expansion	Across Flow : 23 to 150°C	ISO 11359-2	5.0E-5 cm/cm/°C
Linear coefficient of thermal expansion		Flow : 23 to 150°C	ISO 11359-2	5.0E-5 cm/cm/°C
Hot deformation temperature	1.8 MPa, Unannealed, 4.00 mm, 100 mm Span	ISO 75-2/Ae	190 °C
Vicat softening temperature	--	ISO 306/B50	211 °C
RTI Elec		UL 746	170 °C
RTI Imp		UL 746	170 °C
Vicat softening temperature	--	ISO 306/A50	215 °C
RTI		UL 746	170 °C
thermal conductivity		ISO 8302	0.21 W/m/K
Hot deformation temperature	0.45 MPa, Unannealed, 4.00 mm, 100 mm Span	ISO 75-2/Be	195 °C
Vicat softening temperature	--	ISO 306/B120	212 °C
Ball Pressure Test	123 to 127°C	IEC 60695-10-2	通过
injection	Test Condition	Test Method	SABIC INNOVATIVE US/1010M-1100
Temperature at the front of the material cylinder			370 to 420 °C
Mold temperature			140 to 180 °C
Processing (melt) temperature			370 to 410 °C
Suggested maximum moisture content			0.020 %
Spray nozzle temperature			360 to 410 °C
drying temperature			150 °C
Temperature in the middle of the barrel			360 to 410 °C
drying time			4.0 to 6.0 hr
Hopper temperature			80 to 120 °C
Temperature at the rear of the barrel			350 to 400 °C
flammability	Test Condition	Test Method	SABIC INNOVATIVE US/1010M-1100
Extreme Oxygen Index		ISO 4589-2	47 %
UL flame retardant rating	3.0 mm	UL 94	5VA
UL flame retardant rating		0.75 mm	UL 94	V-0
Burning wire flammability index	3.2 mm	IEC 60695-2-12	960 °C
Physical properties	Test Condition	Test Method	SABIC INNOVATIVE US/1010M-1100
Melt Volume Flow Rate (MVR)	340°C/5.0 kg	ISO 1133	13.0 cm3/10min
Water absorption rate	Saturation, 23°C	ISO 62	1.3 %
Shrinkage rate	Flow	Internal Method	0.50 - 0.70 %
Water absorption rate	Equilibrium, 23°C, 50% RH	ISO 62	0.70 %
Electrical performance	Test Condition	Test Method	SABIC INNOVATIVE US/1010M-1100
Compared to the anti leakage trace index	Solution B	IEC 60112	PLC 4
Volume resistivity		IEC 60093	1.0E+15 ohms·cm
Dissipation factor	2.45 GHz	IEC 60250	2.5E-3
Relative permittivity	1 MHz	IEC 60250	2.90
Surface resistivity		IEC 60093	> 1.0E+15 ohms
Dielectric strength	1.60 mm, in Oil	IEC 60243-1	28 KV/mm
Dissipation factor	50 Hz	IEC 60250	5.0E-4
Relative permittivity	60 Hz	IEC 60250	2.90
Dissipation factor	60 Hz	IEC 60250	5.0E-4
Dissipation factor		1 MHz	IEC 60250	6.0E-3
Relative permittivity	50 Hz	IEC 60250	2.90
Compared to the anti leakage trace index	--	IEC 60112	PLC 4
impact performance	Test Condition	Test Method	SABIC INNOVATIVE US/1010M-1100
Suspended wall beam without notch impact strength	23°C	ISO 180/1U	无断裂
Impact strength of cantilever beam gap	23°C	ISO 180/1A	5.0 kJ/m²
Impact strength of cantilever beam gap		-30°C	ISO 180/1A	5.0 kJ/m²
Suspended wall beam without notch impact strength	-30°C	ISO 180/1U	无断裂
hardness	Test Condition	Test Method	SABIC INNOVATIVE US/1010M-1100
Ball Pressure Test	H 358/30	ISO 2039-1	140 Mpa