PEI 1010M-1100 SABIC INNOVATIVE US

129

Form：Granules | Grade：Injection grade

Properties:

High temperature resistantransparentenhanceFlame retardant

Typical Applications:

Food service sector

Supplier(2)

Product Description

Certificates(0)

Datasheet

Product Description

Typical Applications:	Food service sector
Properties:	High temperature resistan \| transparent \| enhance \| Flame retardant

Certificates

No Data...

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Impact strength of cantilever beam gap	-30°C	ISO 180/1A	5.0	kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C	ISO 180/1A	5.0	kJ/m²
Suspended wall beam without notch impact strength	-30°C	ISO 180/1U	无断裂
Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength	23°C	ISO 180/1U	无断裂
flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating	0.75 mm	UL 94	V-0
UL flame retardant rating	UL flame retardant rating	3.0 mm	UL 94	5VA
Burning wire flammability index	3.2 mm	IEC 60695-2-12	960	°C
Extreme Oxygen Index		ISO 4589-2	47	%
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Tensile modulus		ISO 527-2/1	3200	Mpa
tensile strength	Yield	ISO 527-2/50	105	Mpa
tensile strength	tensile strength	Break	ISO 527-2/50	85.0	Mpa
Tensile strain	Yield	ISO 527-2/50	6.0	%
Tensile strain	Tensile strain	Break	ISO 527-2/50	60	%
Bending modulus		ISO 178	3300	Mpa
bending strength		ISO 178	160	Mpa
Taber abraser	1000 Cycles, 1000 g, CS-17 Wheel	Internal Method	10.0	mg
injection	Test Condition	Test Method	Test Result	Test Unit
drying temperature			150	°C
drying time			4.0 to 6.0	hr
Suggested maximum moisture content			0.020	%
Hopper temperature			80 to 120	°C
Temperature at the rear of the barrel			350 to 400	°C
Temperature in the middle of the barrel			360 to 410	°C
Temperature at the front of the material cylinder			370 to 420	°C
Spray nozzle temperature			360 to 410	°C
Processing (melt) temperature			370 to 410	°C
Mold temperature			140 to 180	°C
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Hot deformation temperature	0.45 MPa, Unannealed, 4.00 mm, 100 mm Span	ISO 75-2/Be	195	°C
Hot deformation temperature	Hot deformation temperature	1.8 MPa, Unannealed, 4.00 mm, 100 mm Span	ISO 75-2/Ae	190	°C
Vicat softening temperature	--	ISO 306/A50	215	°C
	Vicat softening temperature	--	ISO 306/B50	211	°C
	Vicat softening temperature	Vicat softening temperature	--	ISO 306/B120	212	°C
Ball Pressure Test	123 to 127°C	IEC 60695-10-2	通过
Linear coefficient of thermal expansion	Flow : 23 to 150°C	ISO 11359-2	5.0E-5	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Across Flow : 23 to 150°C	ISO 11359-2	5.0E-5	cm/cm/°C
thermal conductivity		ISO 8302	0.21	W/m/K
RTI Elec		UL 746	170	°C
RTI Imp		UL 746	170	°C
RTI		UL 746	170	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Melt Volume Flow Rate (MVR)	340°C/5.0 kg	ISO 1133	13.0	cm3/10min
Shrinkage rate	Flow	Internal Method	0.50 - 0.70	%
Water absorption rate	Saturation, 23°C	ISO 62	1.3	%
Water absorption rate	Water absorption rate	Equilibrium, 23°C, 50% RH	ISO 62	0.70	%
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Surface resistivity		IEC 60093	> 1.0E+15	ohms
Volume resistivity		IEC 60093	1.0E+15	ohms·cm
Dielectric strength	1.60 mm, in Oil	IEC 60243-1	28	KV/mm
Relative permittivity	50 Hz	IEC 60250	2.90
	Relative permittivity	60 Hz	IEC 60250	2.90
	Relative permittivity	Relative permittivity	1 MHz	IEC 60250	2.90
Dissipation factor	50 Hz	IEC 60250	5.0E-4
	Dissipation factor	60 Hz	IEC 60250	5.0E-4
		Dissipation factor	1 MHz	IEC 60250	6.0E-3
		Dissipation factor	Dissipation factor	2.45 GHz	IEC 60250	2.5E-3
Compared to the anti leakage trace index	--	IEC 60112	PLC 4
Compared to the anti leakage trace index	Compared to the anti leakage trace index	Solution B	IEC 60112	PLC 4
hardness	Test Condition	Test Method	Test Result	Test Unit
Ball Pressure Test	H 358/30	ISO 2039-1	140	Mpa

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Supplier Join

Get App

Top

PEI 1010M-1100 SABIC INNOVATIVE US

Product Description

Certificates

Technical Data Sheet

Sourcing & Prices

Selling & Verification

Explore Materials

Price Index