Product Name / Manufacturer / Model

Reference Price

PA12 ARKEMA USA 6333 SP 01

US$ 15,350 / MT

FOB Guangzhou port, China

thermal performance	Test Condition	Test Method	ARKEMA USA/6333 SP 01
Hot deformation temperature	0.45 MPa, Unannealed	ISO 75-2/B	90.0 °C
Linear coefficient of thermal expansion	Flow	ISO 11359-2	1.4E-4 cm/cm/°C
Melting temperature		ISO 11357-3	169 °C
Vicat softening temperature		ISO 306/B50	157 °C
squeeze out	Test Condition	Test Method	ARKEMA USA/6333 SP 01
Melt Temperature			210 to 240 °C
drying time			4.0 to 6.0 hr
drying temperature			65 to 75 °C
mechanical properties	Test Condition	Test Method	ARKEMA USA/6333 SP 01
tensile strength	100% Strain	ISO 527-2	17.0 Mpa
Tensile strain	Break	ISO 527-2	> 300 %
tensile strength	Break	ISO 527-2	53.0 Mpa
Tensile modulus		ISO 527-2	307 Mpa
Tensile strain	Yield	ISO 527-2	22 %
tensile strength	10% Strain	ISO 527-2	14.0 Mpa
Nominal tensile fracture strain		ISO 527-2	> 50 %
tensile strength	Yield	ISO 527-2	19.0 Mpa
Wear resistance		ISO 4649	55.0 mm³
Filling analysis	Test Condition	Test Method	ARKEMA USA/6333 SP 01
Melt density			0.830 g/cm³
Specific Heat Capacity of Melt			2800 J/kg/°C
Thermal conductivity of melt			0.18 W/m/K
Physical properties	Test Condition	Test Method	ARKEMA USA/6333 SP 01
Water absorption rate	Equilibrium, 23°C, 50% RH	ISO 62	0.70 %
Shrinkage rate	Flow	ISO 294-4	1.2 %
Shrinkage rate		横向Flow	ISO 294-4	1.4 %
Water absorption rate	Saturation, 23°C	ISO 62	1.1 %
flammability	Test Condition	Test Method	ARKEMA USA/6333 SP 01
Extreme Oxygen Index		ISO 4589-2	20 %
Flammability level		UL 94	HB
injection	Test Condition	Test Method	ARKEMA USA/6333 SP 01
Mold temperature			25 to 60 °C
Processing (melt) temperature			230 to 290 °C
drying temperature			65 to 75 °C
drying time			4.0 to 6.0 hr
elastomer	Test Condition	Test Method	ARKEMA USA/6333 SP 01
Permanent compression deformation	23°C	ISO 815	47 %
tear strength		ISO 34-1	130 kN/m
impact performance	Test Condition	Test Method	ARKEMA USA/6333 SP 01
Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	无断裂
Impact strength of simply supported beam without notch		-30°C	ISO 179/1eU	无断裂
Electrical performance	Test Condition	Test Method	ARKEMA USA/6333 SP 01
Volume resistivity		IEC 60093	9.0E+13 ohms·cm
Dissipation factor	1 MHz	IEC 60250	0.076
Relative permittivity	100 Hz	IEC 60250	9.00
Relative permittivity		1 MHz	IEC 60250	4.00
Surface resistivity		IEC 60093	-- ohms
Dissipation factor	100 Hz	IEC 60250	0.14
Dielectric strength		IEC 60243-1	43 KV/mm
hardness	Test Condition	Test Method	ARKEMA USA/6333 SP 01
Shore hardness	Shore D, 15 Sec	ISO 7619-1	58