'%20/%3e%3cg%20opacity='1'%20transform='translate(150.5%200)%20rotate(0)'%3e%3cpath%20id='路径%204'%20fill-rule='evenodd'%20style='fill:%23C70000'%20opacity='1'%20d='M494%20472.601L487%20410.101L460%20472.601L494%20472.601Z'%3e%3c/path%3e%3cpath%20id='路径%203'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M80%20620.761C152%20676.261%20250%20670.761%20264.5%20670.761C351%20664.261%20412.5%20636.261%20443.5%20620.761C536%20572.261%20580.45%20516.261%20599.5%20492.261C566.05%20492.261%20483.5%20492.261%20465.5%20492.261C408%20532.761%20385.5%20541.761%20369%20550.261C262.5%20599.761%20214%20591.261%20184%20591.261C81%20584.761%2024.3%20510.211%200%20478.261C23%20580.261%2067.5%20609.261%2080%20620.761Z'%3e%3c/path%3e%3cpath%20id='路径%202'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M427.998%202.26C325.498%2014.26%20222.068%2073.64%20247.998%2063.76C384.498%2011.76%20427.998%2024.76%20437.998%2024.76C526.998%2041.76%20559.998%2085.76%20568.998%2095.76C606.498%20142.26%20611.398%20187.06%20613.498%20206.26C631.458%20206.26%20679.498%20206.26%20703.998%20206.26C692.998%20109.26%20633.378%2063.91%20622.998%2056.26C563.998%2012.76%20513.248%205.41%20491.498%202.26C467.498%20-2.24%20437.168%201.19%20427.998%202.26Z'%3e%3c/path%3e%3cpath%20id='路径%201'%20fill-rule='evenodd'%20style='fill:%23C70000'%20opacity='1'%20d='M232%20206.763C243%20178.763%20262%20156.763%20273.5%20140.263C329%2080.2634%20374%2069.7634%20410.5%2061.2634C446.5%2052.2634%20499%2061.2634%20504.5%2061.2634C446%2039.7634%20393%2040.7634%20387.5%2040.7634C308.5%2047.2634%20259.5%2075.2634%20237%2088.7634C162.5%20135.263%20122.95%20185.313%20106%20206.763C139.86%20206.763%20221.5%20206.763%20232%20206.763Z'%3e%3c/path%3e%3c/g%3e%3cpath%20id='减去顶层'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M379.519,227.698l4.237,4.101l-38.576,198.188h98.804l3.966,3.839l-7.614,38.817h-147.091l-4.064,-3.934l46.975,-241.011zM900.883,363.706c-21,-8.75%20-34.89067,-17.22667%20-41.672,-25.43c-6.78133,-8.20333%20-10.172,-19.19533%20-10.172,-32.976c0,-24.06267%208.832,-43.75033%2026.496,-59.063c17.664,-15.312%2040.55067,-22.968%2068.66,-22.968c11.266,0%2022.231,1.121%2032.895,3.363c10.664,2.242%2020.974,5.60533%2030.93,10.09l-8.139,40.672l-5.05,2.827c-6.54467,-5.18467%20-13.96233,-9.21167%20-22.253,-12.081c-9.95333,-3.44533%20-21.00033,-5.168%20-33.141,-5.168c-12.906,0%20-23.406,3.08967%20-31.5,9.269c-8.09333,6.18%20-12.14,14.08233%20-12.14,23.707c0,9.18733%2010.06233,18.32%2030.187,27.398l1.149,0.493l19.031,8.367c15.96867,7.10933%2027.64433,15.668%2035.027,25.676c7.38267,10.00733%2011.074,22.28467%2011.074,36.832c0,25.156%20-8.80467,45.226%20-26.414,60.21c-17.60933,14.98467%20-41.39833,22.477%20-71.367,22.477c-12.03133,0%20-24.30867,-1.422%20-36.832,-4.266c-12.52333,-2.84333%20-25.56633,-7.16367%20-39.129,-12.961l8.62,-44.559l4.63,-2.592c9.52333,7.45333%2019.435,13.24467%2029.735,17.374c11.59333,4.64867%2023.24167,6.973%2034.945,6.973c14.54667,0%2025.97633,-3.19933%2034.289,-9.598c8.31267,-6.39867%2012.469,-15.06667%2012.469,-26.004c0,-6.78133%20-1.914,-12.66%20-5.742,-17.636c-3.82867,-4.97667%20-9.51633,-9.051%20-17.063,-12.223zM54.3672,227.698h68.9058c25.81267,0%2045.473,5.004%2058.981,15.012c13.50733,10.008%2020.261,24.58233%2020.261,43.723c0,12.46867%20-1.996,24.82767%20-5.988,37.077c-3.992,12.25%20-9.16,21.98467%20-15.504,29.204c-8.53133,9.95267%20-19.14067,17.14433%20-31.828,21.575c-12.68733,4.42867%20-29.14817,6.643%20-49.3825,6.643h-26.9063l-17.8828,91.711h-43.7778l-3.88732,-3.761zM642.062,227.698h59.063l18.238,240.969l-4.109,3.976h-43.66l-2.297,-60.539h-0.041l-1.756,-40.844l-0.04,-0.002l-3.249,-98.607l-41.151,94.615l-0.06,-0.006l-20.5,47.5h0.005l-25.411,57.883h-43.849l-3.589,-3.474zM94.7266,268.386l-13.7813,71.859h23.4607c15.96867,0%2027.918,-3.69133%2035.848,-11.074c7.92933,-7.38267%2011.894,-18.457%2011.894,-33.223c0,-9.95333%20-2.84367,-17.03533%20-8.531,-21.246c-5.68733,-4.21067%20-15.367,-6.316%20-29.039,-6.316z'%3e%3c/path%3e%3c/svg%3e)
PA12 6333 SP 01 ARKEMA USA
203
Form：Granules
Properties:
Low temperature resistancHigh temperature resistan
Typical Applications:
Medical Suppliesdisposable
Product Description
Certificates(0)
Datasheet
Product Description
| Typical Applications: | Medical Supplies | disposable |
| Properties: | Low temperature resistanc | High temperature resistan |
Certificates
No Data...
Technical Data Sheet
| Filling analysis | Test Condition | Test Method | Test Result | Test Unit |
|---|---|---|---|---|
| Melt density | 0.830 | g/cm³ | ||
| Thermal conductivity of melt | 0.18 | W/m/K | ||
| Specific Heat Capacity of Melt | 2800 | J/kg/°C | ||
| impact performance | Test Condition | Test Method | Test Result | Test Unit |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 无断裂 | |
| -30°C | ISO 179/1eU | 无断裂 | ||
| flammability | Test Condition | Test Method | Test Result | Test Unit |
| Flammability level | UL 94 | HB | ||
| Extreme Oxygen Index | ISO 4589-2 | 20 | % | |
| elastomer | Test Condition | Test Method | Test Result | Test Unit |
| Permanent compression deformation | 23°C | ISO 815 | 47 | % |
| tear strength | ISO 34-1 | 130 | kN/m | |
| squeeze out | Test Condition | Test Method | Test Result | Test Unit |
| drying temperature | 65 to 75 | °C | ||
| drying time | 4.0 to 6.0 | hr | ||
| Melt Temperature | 210 to 240 | °C | ||
| mechanical properties | Test Condition | Test Method | Test Result | Test Unit |
| Wear resistance | ISO 4649 | 55.0 | mm³ | |
| Nominal tensile fracture strain | ISO 527-2 | > 50 | % | |
| Tensile strain | Break | ISO 527-2 | > 300 | % |
| Yield | ISO 527-2 | 22 | % | |
| tensile strength | 100% Strain | ISO 527-2 | 17.0 | Mpa |
| 10% Strain | ISO 527-2 | 14.0 | Mpa | |
| Break | ISO 527-2 | 53.0 | Mpa | |
| Yield | ISO 527-2 | 19.0 | Mpa | |
| Tensile modulus | ISO 527-2 | 307 | Mpa | |
| injection | Test Condition | Test Method | Test Result | Test Unit |
| drying temperature | 65 to 75 | °C | ||
| drying time | 4.0 to 6.0 | hr | ||
| Processing (melt) temperature | 230 to 290 | °C | ||
| Mold temperature | 25 to 60 | °C | ||
| thermal performance | Test Condition | Test Method | Test Result | Test Unit |
| Linear coefficient of thermal expansion | Flow | ISO 11359-2 | 1.4E-4 | cm/cm/°C |
| Melting temperature | ISO 11357-3 | 169 | °C | |
| Vicat softening temperature | ISO 306/B50 | 157 | °C | |
| Hot deformation temperature | 0.45 MPa, Unannealed | ISO 75-2/B | 90.0 | °C |
| Physical properties | Test Condition | Test Method | Test Result | Test Unit |
| Water absorption rate | Equilibrium, 23°C, 50% RH | ISO 62 | 0.70 | % |
| Saturation, 23°C | ISO 62 | 1.1 | % | |
| Shrinkage rate | Flow | ISO 294-4 | 1.2 | % |
| 横向Flow | ISO 294-4 | 1.4 | % | |
| Electrical performance | Test Condition | Test Method | Test Result | Test Unit |
| Dielectric strength | IEC 60243-1 | 43 | KV/mm | |
| Volume resistivity | IEC 60093 | 9.0E+13 | ohms·cm | |
| Surface resistivity | IEC 60093 | -- | ohms | |
| Relative permittivity | 100 Hz | IEC 60250 | 9.00 | |
| 1 MHz | IEC 60250 | 4.00 | ||
| Dissipation factor | 100 Hz | IEC 60250 | 0.14 | |
| 1 MHz | IEC 60250 | 0.076 | ||
| hardness | Test Condition | Test Method | Test Result | Test Unit |
| Shore hardness | Shore D, 15 Sec | ISO 7619-1 | 58 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.