POM DUPONT USA 527UV NC

Injection grade

US$ 4,410 / MT

FOB Guangzhou port, China

flammability	Test Condition	Test Method	DUPONT USA/527UV NC
UL flame retardant rating	0.8mm	UL 94	HB
Burning rate	1.00mm	ISO 3795	21 mm/min
Atomization	F-value(refraction)4	ISO 6452	90 %
Atomization		G-value(condensate)	ISO 6452	2E-04 g
UL flame retardant rating	0.8mm	IEC 60695-11-10,-20	HB
FMVSS flammability		FMVSS302	B
Supplementary Information	Test Condition	Test Method	DUPONT USA/527UV NC
EmissionofOrganicCompounds		VDA277	16.0 µgC/g
Odor		VDA270	6.00
Emission		VDA275	<8.00 mg/kg
mechanical properties	Test Condition	Test Method	DUPONT USA/527UV NC
bending strength		ISO 178	77.0 Mpa
Poisson's ratio		ISO 527	0.37
Tensile modulus		ISO 527-2	3100 Mpa
Tensile strain	Yield	ISO 527-2	17 %
Nominal tensile fracture strain		ISO 527-2	30 %
tensile strength	Yield	ISO 527-2	70.0 Mpa
Bending modulus		ISO 178	3000 Mpa
thermal performance	Test Condition	Test Method	DUPONT USA/527UV NC
Vicat softening temperature	--	ISO 306/B50	160 °C
Linear coefficient of thermal expansion	MD	ISO 11359-2	1.1E-04 cm/cm/°C
Vicat softening temperature	--	ISO 306/A50	174 °C
AnnealingTime-Optional			30.0 min/mm
Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	163 °C
Linear coefficient of thermal expansion	TD	ISO 11359-2	1.2E-04 cm/cm/°C
AnnealingTemperature			160 °C
Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	95.0 °C
Melting temperature		ISO 11357-3	178 °C
Physical properties	Test Condition	Test Method	DUPONT USA/527UV NC
Water absorption rate	23°C,24hr	ISO 62	0.50 %
density		ISO 1183	1.42 g/cm³
melt mass-flow rate	190°C/2.16kg	ISO 1133	15 g/10min
Shrinkage rate	MD	ISO 294-4	2.0 %
Water absorption rate	Saturation,23°C,2.00mm	ISO 62	1.2 %
Water absorption rate		Equilibrium,23°C,2.00mm,50%RH	ISO 62	0.20 %
Melt Volume Flow Rate (MVR)	190°C/2.16kg	ISO 1133	13.0 cm3/10min
Shrinkage rate	TD	ISO 294-4	1.9 %
impact performance	Test Condition	Test Method	DUPONT USA/527UV NC
Charpy Notched Impact Strength	-30°C	ISO 179/1eA	8.0 kJ/m²
Impact strength of cantilever beam gap	23°C	ISO 180/1A	8.0 kJ/m²
Impact strength of cantilever beam gap		-40°C	ISO 180/1A	8.0 kJ/m²
Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	260 kJ/m²
Impact strength of simply supported beam without notch		-30°C	ISO 179/1eU	260 kJ/m²
Charpy Notched Impact Strength	23°C	ISO 179/1eA	9.0 kJ/m²
Electrical performance	Test Condition	Test Method	DUPONT USA/527UV NC
Dissipation factor	100Hz	IEC 60250	2.1E-03
Compared to the anti leakage trace index		IEC 60112	PLC 0
Volume resistivity		IEC 60093	>1.0E+15 ohms·cm
Dissipation factor	1MHz	IEC 60250	5.6E-03
Relative permittivity	100Hz	IEC 60250	3.80
Surface resistivity		IEC 60093	2E+13 ohms
Relative permittivity	1MHz	IEC 60250	3.80
hardness	Test Condition	Test Method	DUPONT USA/527UV NC
Rockwell hardness	M-Sale	ISO 2039-2	92
Rockwell hardness		R-Sale	ISO 2039-2	120