'%20/%3e%3cg%20opacity='1'%20transform='translate(150.5%200)%20rotate(0)'%3e%3cpath%20id='路径%204'%20fill-rule='evenodd'%20style='fill:%23C70000'%20opacity='1'%20d='M494%20472.601L487%20410.101L460%20472.601L494%20472.601Z'%3e%3c/path%3e%3cpath%20id='路径%203'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M80%20620.761C152%20676.261%20250%20670.761%20264.5%20670.761C351%20664.261%20412.5%20636.261%20443.5%20620.761C536%20572.261%20580.45%20516.261%20599.5%20492.261C566.05%20492.261%20483.5%20492.261%20465.5%20492.261C408%20532.761%20385.5%20541.761%20369%20550.261C262.5%20599.761%20214%20591.261%20184%20591.261C81%20584.761%2024.3%20510.211%200%20478.261C23%20580.261%2067.5%20609.261%2080%20620.761Z'%3e%3c/path%3e%3cpath%20id='路径%202'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M427.998%202.26C325.498%2014.26%20222.068%2073.64%20247.998%2063.76C384.498%2011.76%20427.998%2024.76%20437.998%2024.76C526.998%2041.76%20559.998%2085.76%20568.998%2095.76C606.498%20142.26%20611.398%20187.06%20613.498%20206.26C631.458%20206.26%20679.498%20206.26%20703.998%20206.26C692.998%20109.26%20633.378%2063.91%20622.998%2056.26C563.998%2012.76%20513.248%205.41%20491.498%202.26C467.498%20-2.24%20437.168%201.19%20427.998%202.26Z'%3e%3c/path%3e%3cpath%20id='路径%201'%20fill-rule='evenodd'%20style='fill:%23C70000'%20opacity='1'%20d='M232%20206.763C243%20178.763%20262%20156.763%20273.5%20140.263C329%2080.2634%20374%2069.7634%20410.5%2061.2634C446.5%2052.2634%20499%2061.2634%20504.5%2061.2634C446%2039.7634%20393%2040.7634%20387.5%2040.7634C308.5%2047.2634%20259.5%2075.2634%20237%2088.7634C162.5%20135.263%20122.95%20185.313%20106%20206.763C139.86%20206.763%20221.5%20206.763%20232%20206.763Z'%3e%3c/path%3e%3c/g%3e%3cpath%20id='减去顶层'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M379.519,227.698l4.237,4.101l-38.576,198.188h98.804l3.966,3.839l-7.614,38.817h-147.091l-4.064,-3.934l46.975,-241.011zM900.883,363.706c-21,-8.75%20-34.89067,-17.22667%20-41.672,-25.43c-6.78133,-8.20333%20-10.172,-19.19533%20-10.172,-32.976c0,-24.06267%208.832,-43.75033%2026.496,-59.063c17.664,-15.312%2040.55067,-22.968%2068.66,-22.968c11.266,0%2022.231,1.121%2032.895,3.363c10.664,2.242%2020.974,5.60533%2030.93,10.09l-8.139,40.672l-5.05,2.827c-6.54467,-5.18467%20-13.96233,-9.21167%20-22.253,-12.081c-9.95333,-3.44533%20-21.00033,-5.168%20-33.141,-5.168c-12.906,0%20-23.406,3.08967%20-31.5,9.269c-8.09333,6.18%20-12.14,14.08233%20-12.14,23.707c0,9.18733%2010.06233,18.32%2030.187,27.398l1.149,0.493l19.031,8.367c15.96867,7.10933%2027.64433,15.668%2035.027,25.676c7.38267,10.00733%2011.074,22.28467%2011.074,36.832c0,25.156%20-8.80467,45.226%20-26.414,60.21c-17.60933,14.98467%20-41.39833,22.477%20-71.367,22.477c-12.03133,0%20-24.30867,-1.422%20-36.832,-4.266c-12.52333,-2.84333%20-25.56633,-7.16367%20-39.129,-12.961l8.62,-44.559l4.63,-2.592c9.52333,7.45333%2019.435,13.24467%2029.735,17.374c11.59333,4.64867%2023.24167,6.973%2034.945,6.973c14.54667,0%2025.97633,-3.19933%2034.289,-9.598c8.31267,-6.39867%2012.469,-15.06667%2012.469,-26.004c0,-6.78133%20-1.914,-12.66%20-5.742,-17.636c-3.82867,-4.97667%20-9.51633,-9.051%20-17.063,-12.223zM54.3672,227.698h68.9058c25.81267,0%2045.473,5.004%2058.981,15.012c13.50733,10.008%2020.261,24.58233%2020.261,43.723c0,12.46867%20-1.996,24.82767%20-5.988,37.077c-3.992,12.25%20-9.16,21.98467%20-15.504,29.204c-8.53133,9.95267%20-19.14067,17.14433%20-31.828,21.575c-12.68733,4.42867%20-29.14817,6.643%20-49.3825,6.643h-26.9063l-17.8828,91.711h-43.7778l-3.88732,-3.761zM642.062,227.698h59.063l18.238,240.969l-4.109,3.976h-43.66l-2.297,-60.539h-0.041l-1.756,-40.844l-0.04,-0.002l-3.249,-98.607l-41.151,94.615l-0.06,-0.006l-20.5,47.5h0.005l-25.411,57.883h-43.849l-3.589,-3.474zM94.7266,268.386l-13.7813,71.859h23.4607c15.96867,0%2027.918,-3.69133%2035.848,-11.074c7.92933,-7.38267%2011.894,-18.457%2011.894,-33.223c0,-9.95333%20-2.84367,-17.03533%20-8.531,-21.246c-5.68733,-4.21067%20-15.367,-6.316%20-29.039,-6.316z'%3e%3c/path%3e%3c/svg%3e)
POM 527UV NC DUPONT USA
153
Form：Granules | Grade：Injection grade
Properties:
PhotostabilityLow wearWeather resistance
Typical Applications:
Automotive sectorAutomotive interior parts
Product Description
Certificates(1)
Datasheet
Product Description
| Typical Applications: | Automotive sector | Automotive interior parts |
| Properties: | Photostability | Low wear | Weather resistance |
Certificates
Technical Data Sheet
| impact performance | Test Condition | Test Method | Test Result | Test Unit |
|---|---|---|---|---|
| Charpy Notched Impact Strength | -30°C | ISO 179/1eA | 8.0 | kJ/m² |
| 23°C | ISO 179/1eA | 9.0 | kJ/m² | |
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | 260 | kJ/m² |
| 23°C | ISO 179/1eU | 260 | kJ/m² | |
| Impact strength of cantilever beam gap | -40°C | ISO 180/1A | 8.0 | kJ/m² |
| 23°C | ISO 180/1A | 8.0 | kJ/m² | |
| flammability | Test Condition | Test Method | Test Result | Test Unit |
| Burning rate | 1.00mm | ISO 3795 | 21 | mm/min |
| Atomization | G-value(condensate) | ISO 6452 | 2E-04 | g |
| F-value(refraction)4 | ISO 6452 | 90 | % | |
| FMVSS flammability | FMVSS302 | B | ||
| UL flame retardant rating | 0.8mm | IEC 60695-11-10,-20 | HB | |
| 0.8mm | UL 94 | HB | ||
| mechanical properties | Test Condition | Test Method | Test Result | Test Unit |
| Tensile strain | Yield | ISO 527-2 | 17 | % |
| Nominal tensile fracture strain | ISO 527-2 | 30 | % | |
| Bending modulus | ISO 178 | 3000 | Mpa | |
| bending strength | ISO 178 | 77.0 | Mpa | |
| Poisson's ratio | ISO 527 | 0.37 | ||
| Tensile modulus | ISO 527-2 | 3100 | Mpa | |
| tensile strength | Yield | ISO 527-2 | 70.0 | Mpa |
| thermal performance | Test Condition | Test Method | Test Result | Test Unit |
| AnnealingTemperature | 160 | °C | ||
| AnnealingTime-Optional | 30.0 | min/mm | ||
| Linear coefficient of thermal expansion | TD | ISO 11359-2 | 1.2E-04 | cm/cm/°C |
| MD | ISO 11359-2 | 1.1E-04 | cm/cm/°C | |
| Melting temperature | ISO 11357-3 | 178 | °C | |
| Vicat softening temperature | -- | ISO 306/B50 | 160 | °C |
| -- | ISO 306/A50 | 174 | °C | |
| Hot deformation temperature | 1.8MPa,Unannealed | ISO 75-2/A | 95.0 | °C |
| 0.45MPa,Unannealed | ISO 75-2/B | 163 | °C | |
| Physical properties | Test Condition | Test Method | Test Result | Test Unit |
| density | ISO 1183 | 1.42 | g/cm³ | |
| melt mass-flow rate | 190°C/2.16kg | ISO 1133 | 15 | g/10min |
| Melt Volume Flow Rate (MVR) | 190°C/2.16kg | ISO 1133 | 13.0 | cm3/10min |
| Shrinkage rate | TD | ISO 294-4 | 1.9 | % |
| MD | ISO 294-4 | 2.0 | % | |
| Water absorption rate | 23°C,24hr | ISO 62 | 0.50 | % |
| Saturation,23°C,2.00mm | ISO 62 | 1.2 | % | |
| Equilibrium,23°C,2.00mm,50%RH | ISO 62 | 0.20 | % | |
| Electrical performance | Test Condition | Test Method | Test Result | Test Unit |
| Surface resistivity | IEC 60093 | 2E+13 | ohms | |
| Volume resistivity | IEC 60093 | >1.0E+15 | ohms·cm | |
| Relative permittivity | 100Hz | IEC 60250 | 3.80 | |
| 1MHz | IEC 60250 | 3.80 | ||
| Dissipation factor | 100Hz | IEC 60250 | 2.1E-03 | |
| 1MHz | IEC 60250 | 5.6E-03 | ||
| Compared to the anti leakage trace index | IEC 60112 | PLC 0 | ||
| hardness | Test Condition | Test Method | Test Result | Test Unit |
| Rockwell hardness | M-Sale | ISO 2039-2 | 92 | |
| R-Sale | ISO 2039-2 | 120 | ||
| Supplementary Information | Test Condition | Test Method | Test Result | Test Unit |
| Odor | VDA270 | 6.00 | ||
| EmissionofOrganicCompounds | VDA277 | 16.0 | µgC/g | |
| Emission | VDA275 | <8.00 | mg/kg |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.