POM 500AF NC010 POM vs. - Plastic Material Properties Comparison Chart at Plas.com

Material Selector

All

Plastic Materials Additives Masterbatch Material Selector Price Index Trade Data Plastic News About Us

Material Comparison

Add Comparison Model

Select Products for Comparison (1/4)

Highlight Differences

Hide Same

Product Name / Manufacturer / Model

Reference Price

POM DUPONT USA 500AF NC010

US$ 20,030 / MT

FOB Guangzhou port, China

flammability	Test Condition	Test Method	DUPONT USA/500AF NC010
UL flame retardant rating	1.5mm	IEC 60695-11-10,-20	HB
Burning rate	1.00mm	ISO 3795	<100 mm/min
UL flame retardant rating	3.0mm	UL 94	HB
		3.0mm	IEC 60695-11-10,-20	HB
		1.5mm	UL 94	HB
FMVSS flammability		FMVSS302	B
Physical properties	Test Condition	Test Method	DUPONT USA/500AF NC010
density		ISO 1183	1.53 g/cm³
MediumDensity			1.28 g/cm³
Shrinkage rate	MD	ISO 294-4	2.0 %
Water absorption rate	Saturation,23°C,2.00mm	ISO 62	1.0 %
Water absorption rate		Equilibrium,23°C,2.00mm,50%RH	ISO 62	0.20 %
Shrinkage rate	TD	ISO 294-4	1.4 %
impact performance	Test Condition	Test Method	DUPONT USA/500AF NC010
Charpy Notched Impact Strength	-30°C	ISO 179/1eA	3.0 kJ/m²
Impact strength of cantilever beam gap	23°C	ISO 180/1A	3.0 kJ/m²
Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	40 kJ/m²
Impact strength of simply supported beam without notch		-30°C	ISO 179/1eU	35 kJ/m²
Charpy Notched Impact Strength	23°C	ISO 179/1eA	3.0 kJ/m²
mechanical properties	Test Condition	Test Method	DUPONT USA/500AF NC010
Tensile strain	Break	ISO 527-2	10 %
tensile strength	Break	ISO 527-2	50.0 Mpa
Tensile modulus		ISO 527-2	2800 Mpa
Bending modulus		ISO 178	2500 Mpa
thermal performance	Test Condition	Test Method	DUPONT USA/500AF NC010
Linear coefficient of thermal expansion	MD	ISO 11359-2	1.1E-04 cm/cm/°C
AnnealingTime-Optional			30.0 min/mm
Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	160 °C
Linear coefficient of thermal expansion	TD	ISO 11359-2	1E-04 cm/cm/°C
AnnealingTemperature			160 °C
Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	92.0 °C
Melting temperature		ISO 11357-3	178 °C
hardness	Test Condition	Test Method	DUPONT USA/500AF NC010
Rockwell hardness	M-Sale	ISO 2039-2	83
Rockwell hardness		R-Sale	ISO 2039-2	119
Electrical performance	Test Condition	Test Method	DUPONT USA/500AF NC010
Compared to the anti leakage trace index		IEC 60112	PLC 0
Surface resistivity		IEC 60093	>1.0E+15 ohms