PA66 70G30HSLR NC010 PA66 vs. - Plastic Material Properties Comparison Chart at Plas.com

Material Selector

All

Plastic Materials Additives Masterbatch Material Selector Price Index Trade Data Plastic News About Us

Material Comparison

Add Comparison Model

Select Products for Comparison (1/4)

Highlight Differences

Hide Same

Product Name / Manufacturer / Model

Grade

Reference Price

PA66 DUPONT USA 70G30HSLR NC010

Wear resistant grade

US$ 3,630 / MT

FOB Guangzhou port, China

mechanical properties	Test Condition	Test Method	DUPONT USA/70G30HSLR NC010
Tensile creep modulus	1hr	ISO 899-1	-- Mpa
Tensile strain	Break	ISO 527-2	3.3 %
tensile strength	Break	ISO 527-2	200 Mpa
Tensile modulus		ISO 527-2	10000 Mpa
Tensile creep modulus	1000hr	ISO 899-1	-- Mpa
Supplementary Information	Test Condition	Test Method	DUPONT USA/70G30HSLR NC010
EmissionofOrganicCompounds		VDA277	3.20 µgC/g
Odor		VDA270	4.50
flammability	Test Condition	Test Method	DUPONT USA/70G30HSLR NC010
UL flame retardant rating	1.5mm	IEC 60695-11-10,-20	HB
UL flame retardant rating		0.75mm	UL 94	HB
Extreme Oxygen Index		ISO 4589-2	24 %
Burning rate	1.00mm	ISO 3795	24 mm/min
Atomization	G-value(condensate)	ISO 6452	3E-04 g
Atomization		F-value(refraction)	ISO 6452	95 %
UL flame retardant rating	1.5mm	UL 94	HB
FMVSS flammability		FMVSS302	SE/B
UL flame retardant rating	0.75mm	IEC 60695-11-10,-20	HB
thermal performance	Test Condition	Test Method	DUPONT USA/70G30HSLR NC010
Linear coefficient of thermal expansion	TD：EffectiveThermalDiffusivity	ISO 11359-2	1.1E-07 m²/s
		MD：-40to23°C	ISO 11359-2	2.6E-05 cm/cm/°C
		MD：--	ISO 11359-2	2.6E-05 cm/cm/°C
		MD：55to160°C	ISO 11359-2	1.3E-05 cm/cm/°C
		TD：--	ISO 11359-2	8E-05 cm/cm/°C
Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	261 °C
Glass transition temperature		ISO 11357-2	80.0 °C
Linear coefficient of thermal expansion	TD：55to160°C	ISO 11359-2	1.3E-04 cm/cm/°C
Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	253 °C
Linear coefficient of thermal expansion	TD：-40to23°C	ISO 11359-2	7E-05 cm/cm/°C
Melting temperature		ISO 11357-3	262 °C
Vicat softening temperature		ISO 306/B50	250 °C
Physical properties	Test Condition	Test Method	DUPONT USA/70G30HSLR NC010
MediumDensity			1.20 g/cm³
Shrinkage rate	MD	ISO 294-4	0.30 %
Water absorption rate	Saturation,23°C,2.00mm	ISO 62	6.0 %
Water absorption rate		Equilibrium,23°C,2.00mm,50%RH	ISO 62	1.9 %
ThermalConductivityofMelt			0.21 W/m/K
Top out temperature			210 °C
SpecificHeatCapacity of Melt			2290 J/kg/°C
Shrinkage rate	TD	ISO 294-4	1.1 %
Electrical performance	Test Condition	Test Method	DUPONT USA/70G30HSLR NC010
Dissipation factor	100Hz	IEC 60250	7E-03
Compared to the anti leakage trace index	3.00mm	UL 746	PLC 1
Compared to the anti leakage trace index			IEC 60112	PLC 1
Volume resistivity		IEC 60093	>1.0E+15 ohms·cm
Dissipation factor	1MHz	IEC 60250	0.015
Relative permittivity	100Hz	IEC 60250	4.30
Surface resistivity		IEC 60093	-- ohms
Relative permittivity	1MHz	IEC 60250	4.10
Dielectric strength		IEC 60243-1	38 KV/mm
impact performance	Test Condition	Test Method	DUPONT USA/70G30HSLR NC010
Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	80 kJ/m²
Impact strength of simply supported beam without notch		-30°C	ISO 179/1eU	70 kJ/m²