Product Name / Manufacturer / Model

Grade

Reference Price

TPEE DUPONT TAIWAN 5526

Injection grade

US$ 8,060 / MT

FOB Kaoshiung port, China

mechanical properties	Test Condition	Test Method	DUPONT TAIWAN/5526
Tensile creep modulus	1hr	ISO 899-1	170 Mpa
Tensile strain	Break	ISO 527-2	>300 %
Tensile modulus		ISO 527-2	190 Mpa
tensile strength	50%Strain	ISO 527-2	14.0 Mpa
Nominal tensile fracture strain		ISO 527-2	780 %
Bending modulus		ISO 178	200 Mpa
Tensile creep modulus	1000hr	ISO 899-1	130 Mpa
Wear resistance		ISO 4649	120 mm³
tensile strength	10%Strain	ISO 527-2	11.0 Mpa
		Break	ISO 527-2	40.0 Mpa
		5.0%Strain	ISO 527-2	6.90 Mpa
Tensile strain	Yield	ISO 527-2	35 %
tensile strength	Yield	ISO 527-2	15.0 Mpa
flammability	Test Condition	Test Method	DUPONT TAIWAN/5526
UL flame retardant rating	1.5mm	IEC 60695-11-10,-20	HB
Extreme Oxygen Index		ISO 4589-2	21 %
UL flame retardant rating	3.0mm	IEC 60695-11-10,-20	HB
UL flame retardant rating		1.5mm	UL 94	HB
Fogging-G-value	condensate	ISO 6452	1E-04 g
UL flame retardant rating	3.0mm	UL 94	HB
Burning rate	1.00mm	ISO 3795	28 mm/min
FMVSS flammability		FMVSS302	SE/B
impact performance	Test Condition	Test Method	DUPONT TAIWAN/5526
Impact strength of cantilever beam gap	23°C	ISO 8256/1	270 kJ/m²
Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	NoBreak
Impact strength of simply supported beam without notch		23°C	ISO 179/1eU	NoBreak
thermal performance	Test Condition	Test Method	DUPONT TAIWAN/5526
Linear coefficient of thermal expansion	TD：EffectiveThermalDiffusivity	ISO 11359-2	9E-08 m²/s
Linear coefficient of thermal expansion		TD：--	ISO 11359-2	2E-04 cm/cm/°C
Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	45.0 °C
Linear coefficient of thermal expansion	TD：-40to23°C	ISO 11359-2	1.7E-04 cm/cm/°C
Melting temperature		ISO 11357-3	203 °C
Vicat softening temperature	--	ISO 306/B50	75.0 °C
Linear coefficient of thermal expansion	MD：-40to23°C	ISO 11359-2	1.8E-04 cm/cm/°C
Brittle temperature		ISO 974	-98.0 °C
Vicat softening temperature	--	ISO 306/A50	180 °C
Linear coefficient of thermal expansion	MD：--	ISO 11359-2	2E-04 cm/cm/°C
Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	65.0 °C
Glass transition temperature		ISO 11357-2	-20.0 °C
Physical properties	Test Condition	Test Method	DUPONT TAIWAN/5526
Water absorption rate	23°C,24hr	ISO 62	0.60 %
Shrinkage rate	MD	ISO 294-4	1.4 %
Water absorption rate	Saturation,23°C,2.00mm	ISO 62	0.60 %
SpecificHeatCapacity of Melt			2110 J/kg/°C
Shrinkage rate	TD	ISO 294-4	1.4 %
MediumDensity			1.04 g/cm³
Water absorption rate	Equilibrium,23°C,2.00mm,50%RH	ISO 62	0.20 %
ThermalConductivityofMelt			0.19 W/m/K
melt mass-flow rate		ISO 1133	18 g/10min
Melt Volume Flow Rate (MVR)	220°C/2.16kg	ISO 1133	17.5 cm3/10min
Electrical performance	Test Condition	Test Method	DUPONT TAIWAN/5526
Dissipation factor	100Hz	IEC 60250	9E-03
Volume resistivity		IEC 60093	4E+13 ohms·cm
Dissipation factor	1MHz	IEC 60250	0.038
Relative permittivity	100Hz	IEC 60250	4.90
Surface resistivity		IEC 60093	>1.0E+15 ohms
Relative permittivity	1MHz	IEC 60250	4.60
Dielectric strength		IEC 60243-1	20 KV/mm
Compared to the anti leakage trace index		IEC 60112	PLC 0
elastomer	Test Condition	Test Method	DUPONT TAIWAN/5526
tear strength	Flow	ISO 34-1	130 kN/m
tear strength		横向Flow	ISO 34-1	130 kN/m
Supplementary Information	Test Condition	Test Method	DUPONT TAIWAN/5526
Odor		VDA270	5.00
hardness	Test Condition	Test Method	DUPONT TAIWAN/5526
Shore hardness	ShoreD,15Sec	ISO 868	51
Shore hardness		ShoreD	ISO 868	55