PA6 CM1007 PA6 vs. - Plastic Material Properties Comparison Chart at Plas.com

Material Selector

All

Plastic Materials Additives Masterbatch Material Selector Price Index Trade Data Plastic News About Us

Material Comparison

Add Comparison Model

Select Products for Comparison (1/4)

Highlight Differences

Hide Same

Product Name / Manufacturer / Model

Grade

Reference Price

PA6 TORAY JAPAN CM1007

Injection grade

US$ 3,240 / MT

FOB Guangzhou port, China

Electrical performance	Test Condition	Test Method	TORAY JAPAN/CM1007
Dielectric constant	103Hz	ASTM D-150	无水｜3.9
Dissipation factor	23°C,1MHz		0.030 0.13
Dielectric constant	23°C,1MHz		3.40 4.50
Arc resistance		sec	120 --
Volume resistivity		ASTM D-257	3.5%水｜1011-1012 Ω.cm
Dielectric constant	50Hz	ASTM D-150	3.5%水｜-
Dielectric strength		kV/mm	20 --
Compared to the anti leakage trace index	CTI	V	PLC 0
Dielectric constant	23°C,50Hz		4.10 9.00
Dissipation factor	23°C,1kHz		0.060 0.11
Dielectric constant	23°C,1kHz		3.90 8.00
Dissipation factor	106Hz	ASTM D-150	无水｜0.03
Dissipation factor		23°C,50Hz		0.070 0.10
Dielectric constant	106Hz	ASTM D-150	3.5%水｜-
Arc resistance	1/8	ASTM D-495	无水｜121 秒
Dielectric strength	1/8	ASTM D-149	3.5%水｜- KV/mm
Volume resistivity		ASTM D257/IEC 60093	10^12-13 Ω.cm
Dissipation factor	103Hz	ASTM D-150	0.06｜-
Dissipation factor		50Hz	ASTM D-150	3.5%水｜-
Volume resistivity		ohms·cm	1.0E+14-1.0E+15 1.0E+11到1.0E+12
Compared to the Leakage Traceability Index (CTI)		UL 746	无水｜≤600 V
Physical properties	Test Condition	Test Method	TORAY JAPAN/CM1007
Water absorption rate	23°C,24hr	%	1.8 --
Shrinkage rate	MD：1.00mm3	%	0.50-1.0 --
density		ASTM D792/ISO 1183	1.13
Water absorption rate		ASTM D570/ISO 62	1.8 %
Taber abraser	1000g,CS-17	ASTM D-1044	无水｜3-4 mg/1000次
Shrinkage rate	MD：3.00mm4	%	1.0-1.6 --
Water absorption rate	Saturation,23°C	%	11 --
thermal performance	Test Condition	Test Method	TORAY JAPAN/CM1007
UL-94 flame retardant grade		UL 94	3.5%水｜-
specific heat		J/kg/°C	1900 --
Melting temperature		差示扫描测热计DSC	225 °C
Hot deformation temperature	4.6kg/cm2	ASTM D-695	3.5%水｜- °C
thermal conductivity			3.5%水｜- Kcal/m·hr·℃
Melting temperature		°C	225 --
Hot deformation temperature	0.45MPa,Unannealed	°C	182 --
specific heat			3.5%水｜- Cal/g·℃
thermal conductivity		W/m/K	0.25 --
Linear coefficient of thermal expansion	MD	cm/cm/°C	8E-05 --
Linear coefficient of thermal expansion			ASTM D-696	3.5%水｜- ×10-5cm/cm/℃
Melting temperature			225 ℃（℉）
impact performance	Test Condition	Test Method	TORAY JAPAN/CM1007
Impact strength of simply supported beam without notch	-40°C		无断裂 --
Impact strength of simply supported beam without notch		23°C		无断裂 --
mechanical properties	Test Condition	Test Method	TORAY JAPAN/CM1007
tensile strength	-40℃，Yield	ASTM D-638	无水｜1130 kg/cm2
bending strength	-40℃	ASTM D-790	3.5%水｜1300 kg/cm2
bending strength			ASTM D790/ISO 178	3.8 kg/cm²(MPa)[Lb/in²]
Tensile strain	Break,23°C	%	35
Rockwell hardness	80℃	ASTM D-785	3.5%水｜- R-标度
Bending modulus	-40°C	MPa	3800 3600
tensile strength	-40°C		110 MPa
shear strength	23°C	MPa	70.0 65.0
tensile strength	23℃，Yield	ASTM D-638	3.5%水｜350 kg/cm2
Bending modulus	23℃	ASTM D-790	3.5%水｜8000 kg/cm2
Rockwell hardness		ASTM D785	80
Bending modulus	80°C	MPa	700 300
Rockwell hardness	23℃	ASTM D-785	3.5%水｜88 R-标度
compressive strength	23℃	ASTM D-695	3.5%水｜- kg/cm2
bending strength	-40°C		135 MPa
tensile strength	80°C	MPa	25.0 20.0
Friction coefficient vs. Metal			0.15to0.20 --
tensile strength	80℃，Yield	ASTM D-638	无水｜270 kg/cm2
bending strength	23°C	MPa	110 40.0
Bending modulus	80℃	ASTM D-790	3.5%水｜3000 kg/cm2
bending strength	80°C	MPa	40.0 25.0
Compressive stress	23°C	MPa	80.0 --
bending strength	23℃	ASTM D-790	3.5%水｜400 kg/cm2
Impact strength of cantilever beam gap	V-Notched1/2，23℃		3.5%水｜40 kg.cm/cm
Bending modulus	-40℃	ASTM D-790	3.5%水｜37000 kg/cm2
Elongation at Break	23℃	ASTM D-638	3.5%水｜< 200 %
tensile strength	23°C	MPa	80.0 35.0
Bending modulus	23°C		2800 MPa
bending strength	80℃	ASTM D-790	3.5%水｜250 kg/cm2
Tensile strain	Yield,23°C	%	2.0 --
tensile strength	23℃，Break		3.5%水｜- kg/cm2
Shear strength	23℃	ASTM D-732	无水｜720 kg/cm2
Taber abraser	1000Cycles	mg	3.00to4.00 --
flammability	Test Condition	Test Method	TORAY JAPAN/CM1007
UL flame retardant rating	0.79mm		V-2 --
hardness	Test Condition	Test Method	TORAY JAPAN/CM1007
Rockwell hardness	R-Sale,23°C		119
Rockwell hardness		R-Sale,80°C		80 --
Basic Performance	Test Condition	Test Method	TORAY JAPAN/CM1007
Water absorption rate	23℃，24hr	ASTM D-570	无水｜1.8 %