'%20/%3e%3cg%20opacity='1'%20transform='translate(150.5%200)%20rotate(0)'%3e%3cpath%20id='路径%204'%20fill-rule='evenodd'%20style='fill:%23C70000'%20opacity='1'%20d='M494%20472.601L487%20410.101L460%20472.601L494%20472.601Z'%3e%3c/path%3e%3cpath%20id='路径%203'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M80%20620.761C152%20676.261%20250%20670.761%20264.5%20670.761C351%20664.261%20412.5%20636.261%20443.5%20620.761C536%20572.261%20580.45%20516.261%20599.5%20492.261C566.05%20492.261%20483.5%20492.261%20465.5%20492.261C408%20532.761%20385.5%20541.761%20369%20550.261C262.5%20599.761%20214%20591.261%20184%20591.261C81%20584.761%2024.3%20510.211%200%20478.261C23%20580.261%2067.5%20609.261%2080%20620.761Z'%3e%3c/path%3e%3cpath%20id='路径%202'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M427.998%202.26C325.498%2014.26%20222.068%2073.64%20247.998%2063.76C384.498%2011.76%20427.998%2024.76%20437.998%2024.76C526.998%2041.76%20559.998%2085.76%20568.998%2095.76C606.498%20142.26%20611.398%20187.06%20613.498%20206.26C631.458%20206.26%20679.498%20206.26%20703.998%20206.26C692.998%20109.26%20633.378%2063.91%20622.998%2056.26C563.998%2012.76%20513.248%205.41%20491.498%202.26C467.498%20-2.24%20437.168%201.19%20427.998%202.26Z'%3e%3c/path%3e%3cpath%20id='路径%201'%20fill-rule='evenodd'%20style='fill:%23C70000'%20opacity='1'%20d='M232%20206.763C243%20178.763%20262%20156.763%20273.5%20140.263C329%2080.2634%20374%2069.7634%20410.5%2061.2634C446.5%2052.2634%20499%2061.2634%20504.5%2061.2634C446%2039.7634%20393%2040.7634%20387.5%2040.7634C308.5%2047.2634%20259.5%2075.2634%20237%2088.7634C162.5%20135.263%20122.95%20185.313%20106%20206.763C139.86%20206.763%20221.5%20206.763%20232%20206.763Z'%3e%3c/path%3e%3c/g%3e%3cpath%20id='减去顶层'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M379.519,227.698l4.237,4.101l-38.576,198.188h98.804l3.966,3.839l-7.614,38.817h-147.091l-4.064,-3.934l46.975,-241.011zM900.883,363.706c-21,-8.75%20-34.89067,-17.22667%20-41.672,-25.43c-6.78133,-8.20333%20-10.172,-19.19533%20-10.172,-32.976c0,-24.06267%208.832,-43.75033%2026.496,-59.063c17.664,-15.312%2040.55067,-22.968%2068.66,-22.968c11.266,0%2022.231,1.121%2032.895,3.363c10.664,2.242%2020.974,5.60533%2030.93,10.09l-8.139,40.672l-5.05,2.827c-6.54467,-5.18467%20-13.96233,-9.21167%20-22.253,-12.081c-9.95333,-3.44533%20-21.00033,-5.168%20-33.141,-5.168c-12.906,0%20-23.406,3.08967%20-31.5,9.269c-8.09333,6.18%20-12.14,14.08233%20-12.14,23.707c0,9.18733%2010.06233,18.32%2030.187,27.398l1.149,0.493l19.031,8.367c15.96867,7.10933%2027.64433,15.668%2035.027,25.676c7.38267,10.00733%2011.074,22.28467%2011.074,36.832c0,25.156%20-8.80467,45.226%20-26.414,60.21c-17.60933,14.98467%20-41.39833,22.477%20-71.367,22.477c-12.03133,0%20-24.30867,-1.422%20-36.832,-4.266c-12.52333,-2.84333%20-25.56633,-7.16367%20-39.129,-12.961l8.62,-44.559l4.63,-2.592c9.52333,7.45333%2019.435,13.24467%2029.735,17.374c11.59333,4.64867%2023.24167,6.973%2034.945,6.973c14.54667,0%2025.97633,-3.19933%2034.289,-9.598c8.31267,-6.39867%2012.469,-15.06667%2012.469,-26.004c0,-6.78133%20-1.914,-12.66%20-5.742,-17.636c-3.82867,-4.97667%20-9.51633,-9.051%20-17.063,-12.223zM54.3672,227.698h68.9058c25.81267,0%2045.473,5.004%2058.981,15.012c13.50733,10.008%2020.261,24.58233%2020.261,43.723c0,12.46867%20-1.996,24.82767%20-5.988,37.077c-3.992,12.25%20-9.16,21.98467%20-15.504,29.204c-8.53133,9.95267%20-19.14067,17.14433%20-31.828,21.575c-12.68733,4.42867%20-29.14817,6.643%20-49.3825,6.643h-26.9063l-17.8828,91.711h-43.7778l-3.88732,-3.761zM642.062,227.698h59.063l18.238,240.969l-4.109,3.976h-43.66l-2.297,-60.539h-0.041l-1.756,-40.844l-0.04,-0.002l-3.249,-98.607l-41.151,94.615l-0.06,-0.006l-20.5,47.5h0.005l-25.411,57.883h-43.849l-3.589,-3.474zM94.7266,268.386l-13.7813,71.859h23.4607c15.96867,0%2027.918,-3.69133%2035.848,-11.074c7.92933,-7.38267%2011.894,-18.457%2011.894,-33.223c0,-9.95333%20-2.84367,-17.03533%20-8.531,-21.246c-5.68733,-4.21067%20-15.367,-6.316%20-29.039,-6.316z'%3e%3c/path%3e%3c/svg%3e)
PA6 CM1007 TORAY JAPAN
161
Form：Granules | Grade：Injection grade
Properties:
Low viscosityHigh mobility
Typical Applications:
Electrical appliances
Product Description
Certificates(0)
Datasheet
Product Description
| Typical Applications: | Electrical appliances |
| Properties: | Low viscosity | High mobility |
Certificates
No Data...
Technical Data Sheet
| impact performance | Test Condition | Test Method | Test Result | Test Unit |
|---|---|---|---|---|
| Impact strength of simply supported beam without notch | -40°C | 无断裂 | -- | |
| 23°C | 无断裂 | -- | ||
| flammability | Test Condition | Test Method | Test Result | Test Unit |
| UL flame retardant rating | 0.79mm | V-2 | -- | |
| Basic Performance | Test Condition | Test Method | Test Result | Test Unit |
| Water absorption rate | 23℃，24hr | ASTM D-570 | 3.5%水｜- | % |
| 23℃，24hr | ASTM D-570 | 无水｜1.8 | % | |
| mechanical properties | Test Condition | Test Method | Test Result | Test Unit |
| tensile strength | 80℃，Yield | ASTM D-638 | 无水｜270 | kg/cm2 |
| 80℃，Yield | ASTM D-638 | 3.5%水｜200 | kg/cm2 | |
| 23℃，Break | 无水｜700 | kg/cm2 | ||
| Shear strength | 23℃ | ASTM D-732 | 3.5%水｜650 | kg/cm2 |
| 23℃ | ASTM D-732 | 无水｜720 | kg/cm2 | |
| bending strength | ASTM D790/ISO 178 | 3.8 | kg/cm²(MPa)[Lb/in²] | |
| Rockwell hardness | ASTM D785 | 80 | ||
| Impact strength of cantilever beam gap | V-Notched1/2，23℃ | 无水｜5 | kg.cm/cm | |
| tensile strength | -40℃，Yield | ASTM D-638 | 无水｜1130 | kg/cm2 |
| -40℃，Yield | ASTM D-638 | 3.5%水｜1000 | kg/cm2 | |
| 23℃，Yield | ASTM D-638 | 3.5%水｜350 | kg/cm2 | |
| 23℃，Yield | ASTM D-638 | 无水｜760 | kg/cm2 | |
| Rockwell hardness | 80℃ | ASTM D-785 | 3.5%水｜- | R-标度 |
| 80℃ | ASTM D-785 | 无水｜80 | R-标度 | |
| tensile strength | 23℃，Break | 3.5%水｜- | kg/cm2 | |
| Impact strength of cantilever beam gap | V-Notched1/2，23℃ | 3.5%水｜40 | kg.cm/cm | |
| Bending modulus | 23℃ | ASTM D-790 | 无水｜25000 | kg/cm2 |
| 23℃ | ASTM D-790 | 3.5%水｜8000 | kg/cm2 | |
| bending strength | -40℃ | ASTM D-790 | 无水｜1400 | kg/cm2 |
| -40℃ | ASTM D-790 | 3.5%水｜1300 | kg/cm2 | |
| Friction coefficient vs. Metal | 0.15to0.20 | -- | ||
| Tensile strain | Break,23°C | % | 35 | |
| Bending modulus | -40°C | MPa | 3800 | 3600 |
| 23°C | 2800 | MPa | ||
| tensile strength | -40°C | 110 | MPa | |
| 23°C | MPa | 80.0 | 35.0 | |
| 80°C | MPa | 25.0 | 20.0 | |
| Tensile strain | Yield,23°C | % | 2.0 | -- |
| bending strength | 80℃ | ASTM D-790 | 无水｜430 | kg/cm2 |
| 80℃ | ASTM D-790 | 3.5%水｜250 | kg/cm2 | |
| 23℃ | ASTM D-790 | 无水｜1000 | kg/cm2 | |
| 23℃ | ASTM D-790 | 3.5%水｜400 | kg/cm2 | |
| compressive strength | 23℃ | ASTM D-695 | 无水｜840 | kg/cm2 |
| 23℃ | ASTM D-695 | 3.5%水｜- | kg/cm2 | |
| Elongation at Break | 23℃ | ASTM D-638 | 无水｜130 | % |
| 23℃ | ASTM D-638 | 3.5%水｜< 200 | % | |
| Bending modulus | 80℃ | ASTM D-790 | 无水｜7000 | kg/cm2 |
| 80℃ | ASTM D-790 | 3.5%水｜3000 | kg/cm2 | |
| -40℃ | ASTM D-790 | 无水｜39000 | kg/cm2 | |
| -40℃ | ASTM D-790 | 3.5%水｜37000 | kg/cm2 | |
| Rockwell hardness | 23℃ | ASTM D-785 | 无水｜119 | R-标度 |
| 23℃ | ASTM D-785 | 3.5%水｜88 | R-标度 | |
| Bending modulus | 80°C | MPa | 700 | 300 |
| bending strength | -40°C | 135 | MPa | |
| 23°C | MPa | 110 | 40.0 | |
| 80°C | MPa | 40.0 | 25.0 | |
| Compressive stress | 23°C | MPa | 80.0 | -- |
| shear strength | 23°C | MPa | 70.0 | 65.0 |
| Taber abraser | 1000Cycles | mg | 3.00to4.00 | -- |
| thermal performance | Test Condition | Test Method | Test Result | Test Unit |
| Melting temperature | 225 | ℃（℉） | ||
| Linear coefficient of thermal expansion | ASTM D-696 | 无水｜8 | ×10-5cm/cm/℃ | |
| Melting temperature | 差示扫描测热计DSC | 225 | °C | |
| thermal conductivity | 无水｜0.18 | Kcal/m·hr·℃ | ||
| 3.5%水｜- | Kcal/m·hr·℃ | |||
| Hot deformation temperature | 4.6kg/cm2 | ASTM D-695 | 无水｜182 | °C |
| 4.6kg/cm2 | ASTM D-695 | 3.5%水｜- | °C | |
| Linear coefficient of thermal expansion | ASTM D-696 | 无水｜0.18 | ×10-5cm/cm/℃ | |
| ASTM D-696 | 3.5%水｜- | ×10-5cm/cm/℃ | ||
| Hot deformation temperature | 0.45MPa,Unannealed | °C | 182 | -- |
| Melting temperature | °C | 225 | -- | |
| Linear coefficient of thermal expansion | MD | cm/cm/°C | 8E-05 | -- |
| specific heat | J/kg/°C | 1900 | -- | |
| thermal conductivity | W/m/K | 0.25 | -- | |
| UL-94 flame retardant grade | UL 94 | 无水｜V-2(1/32") | ||
| UL 94 | 3.5%水｜- | |||
| specific heat | 无水｜0.46 | Cal/g·℃ | ||
| 3.5%水｜- | Cal/g·℃ | |||
| Physical properties | Test Condition | Test Method | Test Result | Test Unit |
| Taber abraser | 1000g,CS-17 | ASTM D-1044 | 3.5%水｜- | mg/1000次 |
| 1000g,CS-17 | ASTM D-1044 | 无水｜3-4 | mg/1000次 | |
| Water absorption rate | ASTM D570/ISO 62 | 1.8 | % | |
| density | ASTM D792/ISO 1183 | 1.13 | ||
| Shrinkage rate | MD：1.00mm3 | % | 0.50-1.0 | -- |
| MD：3.00mm4 | % | 1.0-1.6 | -- | |
| Water absorption rate | 23°C,24hr | % | 1.8 | -- |
| Saturation,23°C | % | 11 | -- | |
| Electrical performance | Test Condition | Test Method | Test Result | Test Unit |
| Compared to the Leakage Traceability Index (CTI) | UL 746 | 3.5%水｜- | V | |
| UL 746 | 无水｜≤600 | V | ||
| Dissipation factor | 106Hz | ASTM D-150 | 3.5%水｜- | |
| 106Hz | ASTM D-150 | 无水｜0.03 | ||
| Dielectric constant | 103Hz | ASTM D-150 | 3.5%水｜- | |
| 103Hz | ASTM D-150 | 无水｜3.9 | ||
| Arc resistance | 1/8 | ASTM D-495 | 3.5%水｜- | 秒 |
| 1/8 | ASTM D-495 | 无水｜121 | 秒 | |
| Volume resistivity | ASTM D257/IEC 60093 | 10^12-13 | Ω.cm | |
| ASTM D-257 | 无水｜1014-1015 | Ω.cm | ||
| ASTM D-257 | 3.5%水｜1011-1012 | Ω.cm | ||
| Dissipation factor | 103Hz | ASTM D-150 | 无水｜0.06 | |
| 103Hz | ASTM D-150 | 0.06｜- | ||
| Dielectric constant | 106Hz | ASTM D-150 | 无水｜3.4 | |
| 106Hz | ASTM D-150 | 3.5%水｜- | ||
| 50Hz | ASTM D-150 | 无水｜4.1 | ||
| 50Hz | ASTM D-150 | 3.5%水｜- | ||
| Dielectric strength | 1/8 | ASTM D-149 | 无水｜20 | KV/mm |
| 1/8 | ASTM D-149 | 3.5%水｜- | KV/mm | |
| Dissipation factor | 50Hz | ASTM D-150 | 无水｜0.07 | |
| 50Hz | ASTM D-150 | 3.5%水｜- | ||
| Volume resistivity | ohms·cm | 1.0E+14-1.0E+15 | 1.0E+11到1.0E+12 | |
| Dielectric strength | kV/mm | 20 | -- | |
| Dielectric constant | 23°C,50Hz | 4.10 | 9.00 | |
| 23°C,1kHz | 3.90 | 8.00 | ||
| 23°C,1MHz | 3.40 | 4.50 | ||
| Dissipation factor | 23°C,50Hz | 0.070 | 0.10 | |
| 23°C,1kHz | 0.060 | 0.11 | ||
| 23°C,1MHz | 0.030 | 0.13 | ||
| Arc resistance | sec | 120 | -- | |
| Compared to the anti leakage trace index | CTI | V | PLC 0 | |
| hardness | Test Condition | Test Method | Test Result | Test Unit |
| Rockwell hardness | R-Sale,23°C | 119 | ||
| R-Sale,80°C | 80 | -- |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.