Product Name / Manufacturer / Model

Grade

Reference Price

PC MITSUBISHI ENGINEERING JAPAN EFR3000 BK

Injection grade

US$ 3,610 / MT

FOB Shenzhen Port

machinability	Test Condition	Test Method	MITSUBISHI ENGINEERING JAPAN/EFR3000 BK
Dry conditions			热风干燥 120℃---約4-8小时
Mold temperature			70-100 °C
Processing temperature			250-280 °C
Screw speed			50-100 rpm
Electrical performance	Test Condition	Test Method	MITSUBISHI ENGINEERING JAPAN/EFR3000 BK
Dielectric strength	3.00mm	IEC 60243-1	18 KV/mm
Surface resistivity		ASTM D257/IEC 60093	6.E+15 Ω
Dissipation factor	100Hz	IEC 60250	6E-04
Dielectric constant		ASTM D150/IEC 60250	3.1
Volume resistivity		IEC 60093	3E+16 ohms·cm
Volume resistivity			ASTM D257/IEC 60093	3.E+14 Ω.cm
Dissipation factor	1MHz	IEC 60250	9E-03
Relative permittivity	100Hz	IEC 60250	3.10
Surface resistivity		IEC 60093	6E+15 ohms
Dielectric strength	1.00mm	IEC 60243-1	31 KV/mm
Relative permittivity	1MHz	IEC 60250	3.10
mechanical properties	Test Condition	Test Method	MITSUBISHI ENGINEERING JAPAN/EFR3000 BK
bending strength		ISO 178	92.0 Mpa
Tensile modulus		ISO 527-2	2300 Mpa
Tensile strain	Yield	ISO 527-2	4.7 %
bending strength		ASTM D790/ISO 178	92 kg/cm²(MPa)[Lb/in²]
Tensile modulus		ASTM D638/ISO 527	2300 kg/cm²(MPa)[Lb/in²]
Elongation at Break		ASTM D638/ISO 527	67 %
Nominal tensile fracture strain		ISO 527-2	67 %
tensile strength	Yield	ISO 527-2	61.0 Mpa
Bending modulus		ISO 178	2500 Mpa
Bending modulus			ASTM D790/ISO 178	2500 kg/cm²(MPa)[Lb/in²]
Physical properties	Test Condition	Test Method	MITSUBISHI ENGINEERING JAPAN/EFR3000 BK
Water absorption rate		ASTM D570/ISO 62	0.24 %
Shrinkage rate	MD:3.20mm		0.50-0.70 %
Shrinkage rate			ASTM D955	0.5 - 0.7 %
melt mass-flow rate	300°C/1.2kg	ISO 1133	22 g/10min
Shrinkage rate	TD:3.20mm		0.50-0.70 %
Shrinkage rate		吸水率(Saturation,23°C)		0.24 %
Melt Volume Flow Rate (MVR)	300°C/1.2kg	ISO 1133	21.0 cm3/10min
density		ASTM D792/ISO 1183	1.19
other	Test Condition	Test Method	MITSUBISHI ENGINEERING JAPAN/EFR3000 BK
characteristic			非溴非磷阻燃不透明
thermal performance	Test Condition	Test Method	MITSUBISHI ENGINEERING JAPAN/EFR3000 BK
Linear coefficient of thermal expansion		ASTM D696/ISO 11359	6.6E-05 mm/mm.℃
Linear coefficient of thermal expansion		MD	ISO 11359-2	6.6E-05 cm/cm/°C
Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	137 °C
Linear coefficient of thermal expansion	TD	ISO 11359-2	6.7E-05 cm/cm/°C
Combustibility (rate)		UL 94	V-0 (1.0mm)
Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	125 °C
impact performance	Test Condition	Test Method	MITSUBISHI ENGINEERING JAPAN/EFR3000 BK
Impact strength of simply supported beam without notch	23°C	ISO 179	NoBreak
flammability	Test Condition	Test Method	MITSUBISHI ENGINEERING JAPAN/EFR3000 BK
UL flame retardant rating	1.0mm	UL 94	V-0