PC EFR3000 BK MITSUBISHI ENGINEERING JAPAN

180

Form：Granules | Grade：Injection grade

Properties:

High mobilityFlame retardant

Typical Applications:

Non specific food

Supplier(2)

Product Description

Certificates(0)

Datasheet

Product Description

Typical Applications:	Non specific food
Properties:	High mobility \| Flame retardant

Certificates

No Data...

Technical Data Sheet

other	Test Condition	Test Method	Test Result	Test Unit
characteristic			非溴非磷阻燃不透明
impact performance	Test Condition	Test Method	Test Result	Test Unit
Impact strength of simply supported beam without notch	23°C	ISO 179	NoBreak
machinability	Test Condition	Test Method	Test Result	Test Unit
Mold temperature			70-100	°C
Screw speed			50-100	rpm
Processing temperature			260-290	°C
	Processing temperature			270-300	°C
	Processing temperature	Processing temperature			250-280	°C
Dry conditions			热风干燥 120℃---約4-8小时
flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating	1.0mm	UL 94	V-0
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Tensile modulus		ISO 527-2	2300	Mpa
tensile strength	Yield	ISO 527-2	61.0	Mpa
Elongation at Break		ASTM D638/ISO 527	67	%
bending strength		ASTM D790/ISO 178	92	kg/cm²(MPa)[Lb/in²]
Bending modulus		ASTM D790/ISO 178	2500	kg/cm²(MPa)[Lb/in²]
Tensile modulus		ASTM D638/ISO 527	2300	kg/cm²(MPa)[Lb/in²]
Tensile strain	Yield	ISO 527-2	4.7	%
Nominal tensile fracture strain		ISO 527-2	67	%
Bending modulus		ISO 178	2500	Mpa
bending strength		ISO 178	92.0	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Linear coefficient of thermal expansion		ASTM D696/ISO 11359	6.6E-05	mm/mm.℃
Combustibility (rate)		UL 94	V-0 (1.0mm)
Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	137	°C
Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	125	°C
Linear coefficient of thermal expansion	MD	ISO 11359-2	6.6E-05	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD	ISO 11359-2	6.7E-05	cm/cm/°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Shrinkage rate	吸水率(Saturation,23°C)		0.24	%
	Shrinkage rate	MD:3.20mm		0.50-0.70	%
	Shrinkage rate	Shrinkage rate	TD:3.20mm		0.50-0.70	%
Melt Volume Flow Rate (MVR)	300°C/1.2kg	ISO 1133	21.0	cm3/10min
melt mass-flow rate	300°C/1.2kg	ISO 1133	22	g/10min
Water absorption rate		ASTM D570/ISO 62	0.24	%
Shrinkage rate		ASTM D955	0.5 - 0.7	%
density		ASTM D792/ISO 1183	1.19
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Volume resistivity		ASTM D257/IEC 60093	3.E+14	Ω.cm
Dielectric constant		ASTM D150/IEC 60250	3.1
Surface resistivity		ASTM D257/IEC 60093	6.E+15	Ω
Surface resistivity	Surface resistivity		IEC 60093	6E+15	ohms
Volume resistivity		IEC 60093	3E+16	ohms·cm
Dielectric strength	1.00mm	IEC 60243-1	31	KV/mm
Dielectric strength	Dielectric strength	3.00mm	IEC 60243-1	18	KV/mm
Relative permittivity	100Hz	IEC 60250	3.10
Relative permittivity	Relative permittivity	1MHz	IEC 60250	3.10
Dissipation factor	100Hz	IEC 60250	6E-04
Dissipation factor	Dissipation factor	1MHz	IEC 60250	9E-03

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Supplier Join

Get App

Top

PC EFR3000 BK MITSUBISHI ENGINEERING JAPAN

Product Description

Certificates

Technical Data Sheet

Sourcing & Prices

Selling & Verification

Explore Materials

Price Index