PC
PC SABIC INNOVATIVE NANSHA HFD1810 NA9E108T
Light diffusion level
US$ 5,120 / MT
FOB Guangzhou port, China
injectionTest ConditionTest MethodSABIC INNOVATIVE NANSHA/HFD1810 NA9E108T
Back pressure0.300 to 0.700 Mpa
Temperature at the front of the material cylinder260 to 305 °C
Mold temperature50 to 80 °C
Screw speed35 to 75 rpm
Processing (melt) temperature260 to 305 °C
Suggested injection volume40 to 60 %
Spray nozzle temperature255 to 300 °C
Exhaust hole depth0.038 to 0.076 mm
drying temperature105 to 110 °C
Temperature in the middle of the barrel250 to 295 °C
drying time3.0 to 4.0 hr
Temperature at the rear of the barrel240 to 280 °C
mechanical propertiesTest ConditionTest MethodSABIC INNOVATIVE NANSHA/HFD1810 NA9E108T
bending strength--5,6ISO 17891.0 Mpa
Bending modulus50.0 mm Span4ASTM D7902240 Mpa
bending strengthYield, 50.0 mm Span4ASTM D790100 Mpa
elongationBreakISO 527-2/5097 %
Yield3ASTM D6385.5 %
YieldISO 527-2/506.0 %
Break3ASTM D638130 %
tensile strengthBreakISO 527-2/5056.0 Mpa
Yield3ASTM D63860.0 Mpa
YieldISO 527-2/5063.0 Mpa
Tensile modulus--2ASTM D6382270 Mpa
--ISO 527-2/12180 Mpa
Bending modulus--5ISO 1782180 Mpa
tensile strengthBreak3ASTM D63856.0 Mpa
optical performanceTest ConditionTest MethodSABIC INNOVATIVE NANSHA/HFD1810 NA9E108T
turbidity2540 μmASTM D1003< 1.0 %
transmissivity2540 μmASTM D100388.0 %
Refractive indexASTM D5421.582
thermal performanceTest ConditionTest MethodSABIC INNOVATIVE NANSHA/HFD1810 NA9E108T
Linear coefficient of thermal expansionAcross Flow : -40 to 40°CASTM E8318.0E-5 cm/cm/°C
Across Flow : -40°CISO 11359-28.0E-5 cm/cm/°C
Hot deformation temperature1.8 MPa, Unannealed, 4.00 mm, 64.0 mm Span9ISO 75-2/Af115 °C
0.45 MPa, Unannealed, 3.20 mmASTM D648121 °C
Linear coefficient of thermal expansionFlow : -40 to 40°CASTM E8318.0E-5 cm/cm/°C
Vicat softening temperature--ISO 306/B50129 °C
RTI ElecUL 746105 °C
RTI ImpUL 746105 °C
RTIUL 746105 °C
Hot deformation temperature1.8 MPa, Unannealed, 3.20 mmASTM D648110 °C
Vicat softening temperature--ISO 306/B120130 °C
Ball Pressure Test123 to 127°CIEC 60695-10-2通过
Vicat softening temperature--ASTM D152510135 °C
Physical propertiesTest ConditionTest MethodSABIC INNOVATIVE NANSHA/HFD1810 NA9E108T
Water absorption rateSaturation, 23°CISO 620.30 %
Melt Volume Flow Rate (MVR)300°C/1.2 kgISO 113338.0 cm3/10min
Water absorption rateEquilibrium, 23°C, 50% RHISO 620.15 %
Shrinkage rate3.20 mm，FlowInternal Method0.50 - 0.70 %
melt mass-flow rate300°C/1.2 kgASTM D123840 g/10 min
impact performanceTest ConditionTest MethodSABIC INNOVATIVE NANSHA/HFD1810 NA9E108T
Impact strength of simply supported beam without notch-30°CISO 179/1eU无断裂
Suspended wall beam without notch impact strength23°CISO 180/1U无断裂
Charpy Notched Impact Strength-30°CISO 179/1eA13 kJ/m²
Dart impact--ISO 6603-295.0 J
Impact strength of simply supported beam without notch23°CISO 179/1eU无断裂
Dart impact23°C, Total EnergyASTM D376356.0 J
Charpy Notched Impact Strength23°CISO 179/1eA64 kJ/m²
Suspended wall beam without notch impact strength-30°CISO 180/1U无断裂
hardnessTest ConditionTest MethodSABIC INNOVATIVE NANSHA/HFD1810 NA9E108T
Rockwell hardnessR-ScaleASTM D785120
flammabilityTest ConditionTest MethodSABIC INNOVATIVE NANSHA/HFD1810 NA9E108T
UL flame retardant rating0.30 mmUL 94HB
1.0 mmUL 94V-2

Supplier Join

Contact Us

Get App

Top

Sourcing & Prices

Selling & Verification

Explore Materials

Price Index

+86 0755 27873515

Room 906, Global Digital Building, No. 9 Gaoxin Middle 3rd Road, Maling Community, Yuehai Subdistrict, Nanshan District, Shenzhen, Guangdong Province, China