PC HFD1810 NA9E108T SABIC INNOVATIVE NANSHA

117

Form：Granules | Grade：Light diffusion level

Properties:

High mobilitycopolymer

Typical Applications:

Automotive sectorElectronic fieldElectrical field

Supplier(2)

Product Description

Certificates(0)

Datasheet

Product Description

Typical Applications:	Automotive sector \| Electronic field \| Electrical field
Properties:	High mobility \| copolymer

Certificates

No Data...

Technical Data Sheet

optical performance	Test Condition	Test Method	Test Result	Test Unit
Refractive index		ASTM D542	1.582
transmissivity	2540 μm	ASTM D1003	88.0	%
turbidity	2540 μm	ASTM D1003	< 1.0	%
impact performance	Test Condition	Test Method	Test Result	Test Unit
Charpy Notched Impact Strength	-30°C	ISO 179/1eA	13	kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	23°C	ISO 179/1eA	64	kJ/m²
Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	无断裂
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	无断裂
Suspended wall beam without notch impact strength	-30°C	ISO 180/1U	无断裂
Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength	23°C	ISO 180/1U	无断裂
Dart impact	23°C, Total Energy	ASTM D3763	56.0	J
Dart impact	Dart impact	--	ISO 6603-2	95.0	J
flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating	0.30 mm	UL 94	HB
UL flame retardant rating	UL flame retardant rating	1.0 mm	UL 94	V-2
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Tensile modulus	--2	ASTM D638	2270	Mpa
Tensile modulus	Tensile modulus	--	ISO 527-2/1	2180	Mpa
tensile strength	Yield3	ASTM D638	60.0	Mpa
	tensile strength	Yield	ISO 527-2/50	63.0	Mpa
		tensile strength	Break3	ASTM D638	56.0	Mpa
		tensile strength	tensile strength	Break	ISO 527-2/50	56.0	Mpa
elongation	Yield3	ASTM D638	5.5	%
	elongation	Yield	ISO 527-2/50	6.0	%
		elongation	Break3	ASTM D638	130	%
		elongation	elongation	Break	ISO 527-2/50	97	%
Bending modulus	50.0 mm Span4	ASTM D790	2240	Mpa
Bending modulus	Bending modulus	--5	ISO 178	2180	Mpa
bending strength	--5,6	ISO 178	91.0	Mpa
bending strength	bending strength	Yield, 50.0 mm Span4	ASTM D790	100	Mpa
injection	Test Condition	Test Method	Test Result	Test Unit
drying temperature			105 to 110	°C
drying time			3.0 to 4.0	hr
Suggested injection volume			40 to 60	%
Temperature at the rear of the barrel			240 to 280	°C
Temperature in the middle of the barrel			250 to 295	°C
Temperature at the front of the material cylinder			260 to 305	°C
Spray nozzle temperature			255 to 300	°C
Processing (melt) temperature			260 to 305	°C
Mold temperature			50 to 80	°C
Back pressure			0.300 to 0.700	Mpa
Screw speed			35 to 75	rpm
Exhaust hole depth			0.038 to 0.076	mm
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Hot deformation temperature	0.45 MPa, Unannealed, 3.20 mm	ASTM D648	121	°C
	Hot deformation temperature	1.8 MPa, Unannealed, 3.20 mm	ASTM D648	110	°C
	Hot deformation temperature	Hot deformation temperature	1.8 MPa, Unannealed, 4.00 mm, 64.0 mm Span9	ISO 75-2/Af	115	°C
Vicat softening temperature	--	ASTM D152510	135	°C
	Vicat softening temperature	--	ISO 306/B50	129	°C
	Vicat softening temperature	Vicat softening temperature	--	ISO 306/B120	130	°C
Ball Pressure Test	123 to 127°C	IEC 60695-10-2	通过
Linear coefficient of thermal expansion	Flow : -40 to 40°C	ASTM E831	8.0E-5	cm/cm/°C
	Linear coefficient of thermal expansion	Across Flow : -40 to 40°C	ASTM E831	8.0E-5	cm/cm/°C
	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Across Flow : -40°C	ISO 11359-2	8.0E-5	cm/cm/°C
RTI Elec		UL 746	105	°C
RTI Imp		UL 746	105	°C
RTI		UL 746	105	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
melt mass-flow rate	300°C/1.2 kg	ASTM D1238	40	g/10 min
Melt Volume Flow Rate (MVR)	300°C/1.2 kg	ISO 1133	38.0	cm3/10min
Shrinkage rate	3.20 mm，Flow	Internal Method	0.50 - 0.70	%
Water absorption rate	Saturation, 23°C	ISO 62	0.30	%
Water absorption rate	Water absorption rate	Equilibrium, 23°C, 50% RH	ISO 62	0.15	%
hardness	Test Condition	Test Method	Test Result	Test Unit
Rockwell hardness	R-Scale	ASTM D785	120

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Supplier Join

Get App