PA66 A 20 V35 PA66 vs. - Plastic Material Properties Comparison Chart at Plas.com

Material Selector

All

Plastic Materials Additives Masterbatch Material Selector Price Index Trade Data Plastic News About Us

Material Comparison

Add Comparison Model

Select Products for Comparison (1/4)

Highlight Differences

Hide Same

Product Name / Manufacturer / Model

Grade

Reference Price

PA66 TECNICA ITALY A 20 V35

Enhanced level

US$ 4,260 / MT

FOB Dongguan Port

flammability	Test Condition	Test Method	TECNICA ITALY/A 20 V35
UL flame retardant rating	1.6 mm	UL 94	V-0
Extreme Oxygen Index		ISO 4589-2	31 %
Burning wire flammability index	1.6 mm	IEC 60695-2-12	960 °C
UL flame retardant rating	0.8 mm	UL 94	V-0
Hot filament ignition temperature	1.6 mm	IEC 60695-2-13	725 °C
UL flame retardant rating	3.2 mm	UL 94	V-0
Burning wire flammability index	0.8 mm	IEC 60695-2-12	960 °C
Burning wire flammability index		3.2 mm	IEC 60695-2-12	960 °C
Physical properties	Test Condition	Test Method	TECNICA ITALY/A 20 V35
Water absorption rate	Equilibrium, 23°C, 50% RH	ISO 62	1.7 %
Water absorption rate		24 hr, 23°C	ISO 62	0.60 %
injection	Test Condition	Test Method	TECNICA ITALY/A 20 V35
Temperature at the front of the material cylinder			280 to 290 °C
Mold temperature			60 to 90 °C
drying temperature			80 °C
Temperature in the middle of the barrel			270 to 280 °C
Suggested maximum moisture content			0.20 %
Temperature at the rear of the barrel			265 to 275 °C
mechanical properties	Test Condition	Test Method	TECNICA ITALY/A 20 V35
bending strength	23°C	ISO 178	260 Mpa
Tensile modulus	23°C	ISO 527-2/1A	12500 Mpa
Bending modulus	23°C	ISO 178	11000 Mpa
Tensile strain	Break, 23°C	ISO 527-2	2.1 %
tensile strength	Break, 23°C	ISO 527-2/1A	175 Mpa
impact performance	Test Condition	Test Method	TECNICA ITALY/A 20 V35
Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	60 kJ/m²
Impact strength of simply supported beam without notch		-30°C	ISO 179/1eU	55 kJ/m²
Electrical performance	Test Condition	Test Method	TECNICA ITALY/A 20 V35
Compared to the anti leakage trace index	Solution A	IEC 60112	PLC 1
Volume resistivity		IEC 60093	1.0E+15 ohms·cm
Dissipation factor		IEC 60250	0.020
Dielectric strength	0.800 mm	IEC 60243-1	32 KV/mm
Relative permittivity		IEC 60250	3.40
Surface resistivity		IEC 60093	1.0E+14 ohms
thermal performance	Test Condition	Test Method	TECNICA ITALY/A 20 V35
Hot deformation temperature	1.8 MPa, Unannealed	ISO 75-2/Af	244 °C
Melting temperature		ISO 11357-3	263 °C