PC
PC SABIC INNOVATIVE US DMX1435-GY6E563T
US$ 8,271 / MT
FOB Guangzhou port, China
optical performanceTest ConditionTest MethodSABIC INNOVATIVE US/DMX1435-GY6E563T
Refractive indexISO 4891.584
turbidity2540PmASTM D10030.8 %
transmissivity2540pmASTM DI 00388 %
Refractive indexASTM D5421.584
mechanical propertiesTest ConditionTest MethodSABIC INNOVATIVE US/DMX1435-GY6E563T
Impact strength of cantilever beam gap23℃ASTM D25630 J/m
bending strengthYield2.0mm/minISO 178108 Mpa
Bending modulus1.3mm/minASTM D7902600 Mpa
Tensile modulus1.0mm/minISO 5272450 Mpa
tensile strength斯裂50mm/minISO 52760 Mpa
Impact strength of cantilever beam gap-30℃ 3.0mmISO 18045 kJ/m²
Instrumented impact23℃总能量ASTM D376330 J
Impact strength of cantilever beam gap-30℃ASTM D25630 J/m
Suspended wall beam without notch impact strength23℃ASTM D4812NB J/m
elongationYield50mm/minISO 5277 %
Erichsen scratch depth6N内部测试方法14 micrometer
Taber wear resistanceCS-17轮1kgASTM D104410 mg/1000cy
elongationBreak50mm/min I型ASTM D63870 %
tensile strengthYield50mm/minISO 52780 Mpa
Impact strength of cantilever beam gap“-30℃ 3.0mm A型NotchedISO 1804 kJ/m²
Charpy Notched Impact Strength23°C 3.0mmISO 179NB kJ/m²
elongationBreak50mm/minISO 52740 %
tensile strengthYield50mm/min I型ASTM D63880 Mpa
Break50mm/mini型ASTM D63865 Mpa
Bending modulus2.0mm/minISO 1782450 Mpa
Charpy Notched Impact Strength23°C3.0mm 1eA型ISO 1793 kJ/m²
Tensile modulus50mm/minASTM D6382900 Mpa
Charpy Notched Impact Strength30℃ 3.0mm 1eA型^ISO 1793 kJ/m²
-30℃ 3.0mmISO 17947 kJ/m²
Taiberten lossCS-17轮1kg内部测试方法10 mg/1000cy
elongationYield50mm/min iI型ASTM D6387 %
Suspended wall beam without notch impact strength23°C 3.0mmISO 180NB kJ/m²
Impact strength of cantilever beam gap23°C 3.0mm A型NotchedISO 1805 kJ/m²
bending strengthYield1.3mm/minASTM D790120 Mpa
Physical propertiesTest ConditionTest MethodSABIC INNOVATIVE US/DMX1435-GY6E563T
densityISO 11831.17 g/cm³
Water absorption rate23℃EquilibriumASTM D5700.28 %
50RH 24hrASTM D5700.04 %
24hrASTM D5700.08 %
23℃SaturationISO 620.27 %
Bi RongASTM D7920.85 cm³/g
Water absorption rate23℃ 50RHISO 620.13 %
melt mass-flow rate300℃ 1.2kgASTM D123814.5 g/10min
Shrinkage rateFlow3.2mm内部测试方法0.5-0.8 %
melt mass-flow rate300℃ 1.2kgISO 113313 cm3/10min
densityASTM D7921.2 g/cm³
Water absorption rate50RHEquilibriumASTM D5700.13 %
hardnessTest ConditionTest MethodSABIC INNOVATIVE US/DMX1435-GY6E563T
Rockwell hardnessM标尺ASTM D78593
Ball Pressure TestH358/30ISO 2039128 Mpa
Rockwell hardnessL标尺ASTM D785108
Pencil hardness1.0kgASTM D3363H
thermal performanceTest ConditionTest MethodSABIC INNOVATIVE US/DMX1435-GY6E563T
Hot deformation temperature0.45MPa 4.0mmISO 75131 °C
Ball indentation testIEC 60695140 °C
Vicat softening temperature120℃/hr 50NISO 306140 °C
Hot deformation temperatureUnannealed1.8MPa 3.2mmASTM D648119 °C
Linear expansion coefficient flow-40.0~95℃ASTM E8310.000070 cm/cm/℃
Linear coefficient of thermal expansionFlow23~80℃ISO 113590.000070 cm/cm/℃
specific heatASTM C3511.4 J/(g.℃)
Vicat softening temperature50℃/hr 50NISO 306138 °C
thermal conductivityASTM C1770.2 w/(m.℃)
Hot deformation temperatureUnannealed0.45MPa 3.2mmASTM D648133 °C
thermal conductivityISO 83020.2 w/(m.℃)
Vertical expansion coefficient-40.0~95℃ASTM E8310.000070 cm/cm/℃
Vicat softening temperature50℃/hr 50NASTM DI 525139 °C
Hot deformation temperature1.8MPa 4.0mmISO 75118 °C
Linear coefficient of thermal expansion垂直23~80℃ISO 113590.000070 cm/cm/℃