PA66 408HS PA66 vs. - Plastic Material Properties Comparison Chart at Plas.com

Material Selector

All

Plastic Materials Additives Masterbatch Material Selector Price Index Trade Data Plastic News About Us

Material Comparison

Add Comparison Model

Select Products for Comparison (1/4)

Highlight Differences

Hide Same

Product Name / Manufacturer / Model

Grade

Certificates

Reference Price

PA66 DUPONT USA 408HS

Special level

US$ 6,090 / MT

FOB Guangzhou port, China

thermal performance	Test Condition	Test Method	DUPONT USA/408HS
Load deformation	13.8MPa，50℃	ASTM D-621	50%RH｜- %
Extreme Oxygen Index		ASTM D2863	23 %
Brittle temperature		ASTM D-746	50%RH｜-84 °C
Linear coefficient of thermal expansion		ASTM D696/ISO 11359	7×10-5 mm/mm.℃
Linear coefficient of thermal expansion		平行Flow	ASTM E831	0.00010 cm/cm/ ℃
Hot deformation temperature	(0.5)×106Pa	ASTM D-648	50%RH｜- °C
Melting temperature	Fisher Johns法	ASTM D-789	255 °C
UL flame retardant rating		UL 94	HB
Linear coefficient of thermal expansion		ASTM D-696	50%RH｜- m/m/℃
Melting temperature		ASTM D-2177	50%RH｜- °C
Hot deformation temperature	66 psi， Unannealed	ASTM D648	184 °C
Melting temperature			255 ℃（℉）
Hot deformation temperature	18×106Pa	ASTM D-648	50%RH｜- °C
Physical properties	Test Condition	Test Method	DUPONT USA/408HS
Water absorption rate		ASTM D570/ISO 62	1.2 %
		24hr	ASTM D570	1.2 %
		Saturation	ASTM D570	7.0 %
density		ASTM D792/ISO 1183	1.09
mechanical properties	Test Condition	Test Method	DUPONT USA/408HS
tensile strength	23℃	ASTM D-638	DAM｜62.1 Mpa
Hardness (Rockwell M)		ASTM D-785	DAM｜M71
Hardness (Rockwell R)		ASTM D-785	DAM｜R115
elongation		ASTM D638/ISO 527	60.7 %
Elongation at Break		ASTM D638	50 %
Impact strength of cantilever beam gap	长试样23℃	ASTM D-1822	DAM｜550 kJ/m²
Impact strength of cantilever beam gap		23℃	ASTM D-256	DAM｜230 J/m
Elongation at Break		ASTM D638/ISO 527	80 %
Elongation at Break		23℃	ASTM D-638	DAM｜80 %
tensile strength	Yield	ASTM D638	62.7 Mpa
Shore hardness		ASTM D-676	DAM｜83
tensile strength	23℃，Yield		50%RH｜51.7 Mpa
Rubbing modulus	23℃	ASTM D-790	DAM｜1965 Mpa
Bending modulus		ASTM D790	2070 Mpa
elongation at yield		ASTM D-638	50%RH｜15 %
Impact strength of cantilever beam gap		ASTM D256	134 J/m
Impact strength of cantilever beam gap		短试样23℃	ASTM D-1822	DAM｜189 kJ/m²
tensile strength		ASTM D638/ISO 527	62.1 kg/cm²(MPa)[Lb/in²]
Basic Performance	Test Condition	Test Method	DUPONT USA/408HS
Water absorption rate	Saturation(23℃)	ASTM D-570	DAM｜7.0 %
Water absorption rate		24hr浸渍(23℃)	ASTM D-570	DAM｜1.2 %
other	Test Condition	Test Method	DUPONT USA/408HS
characteristic			注塑级.良好的热稳定性
Electrical performance	Test Condition	Test Method	DUPONT USA/408HS
Dissipation factor	100Hz(cps)	ASTM D-150	50%RH｜0.1
Volume resistivity		ASTM D-257	DAM｜1013 Ω.m
Dissipation factor	103Hz(cps)	ASTM D-150	50%RH｜0.11
Dissipation factor		106Hz(cps)	ASTM D-150	50%RH｜0.10
Dielectric constant		ASTM D150/IEC 60250	3.1
		103Hz(cps)	ASTM D-150	DAM｜3.1
		100Hz(cps)	ASTM D-150	50%RH｜4.8
Volume resistivity		ASTM D257/IEC 60093	10 Ω.cm
Dielectric constant	106Hz(cps)	ASTM D-150	50%RH｜3.3
Other performance	Test Condition	Test Method	DUPONT USA/408HS
Limiting Oxygen Index (LOI)		ASTM D-2863	50%RH｜20 %