Product Name / Manufacturer / Model

Grade

Certificates

Reference Price

POM DUPONT SHENZHEN 500P

Injection grade

US$ 4,920 / MT

FOB Shenzhen Port

flammability	Test Condition	Test Method	DUPONT SHENZHEN/500P
UL flame retardant rating	0.8mm	UL 94	HB
UL flame retardant rating		1.5mm	IEC 60695-11-10,-20	HB
Burning rate	1.00mm	ISO 3795	24 mm/min
Atomization	G-value(condensate)	ISO 6452	3.5E-04 g
Atomization		F-value(refraction)	ISO 6452	90 %
UL flame retardant rating	0.8mm	IEC 60695-11-10,-20	HB
UL flame retardant rating		1.5mm	UL 94	HB
FMVSS flammability		FMVSS302	B
Supplementary Information	Test Condition	Test Method	DUPONT SHENZHEN/500P
EmissionofOrganicCompounds		VDA277	3.10 µgC/g
Emission		VDA275	<8.00 mg/kg
mechanical properties	Test Condition	Test Method	DUPONT SHENZHEN/500P
Poisson's ratio		ISO 527	0.35
Tensile modulus		ISO 527-2	3100 Mpa
Tensile strain	Yield	ISO 527-2	14 %
Nominal tensile fracture strain		ISO 527-2	25 %
tensile strength	Yield	ISO 527-2	71.0 Mpa
Bending modulus		ISO 178	3000 Mpa
Physical properties	Test Condition	Test Method	DUPONT SHENZHEN/500P
density		ISO 1183	1.42 g/cm³
melt mass-flow rate	190°C/2.16kg	ISO 1133	15 g/10min
Shrinkage rate	MD	ISO 294-4	2.0 %
Water absorption rate	Saturation,23°C,2.00mm	ISO 62	1.3 %
Water absorption rate		Equilibrium,23°C,2.00mm,50%RH	ISO 62	0.40 %
Shrinkage rate	TD	ISO 294-4	1.8 %
impact performance	Test Condition	Test Method	DUPONT SHENZHEN/500P
Charpy Notched Impact Strength	-30°C	ISO 179/1eA	7.0 kJ/m²
Impact strength of cantilever beam gap	23°C	ISO 180/1A	8.0 kJ/m²
Impact strength of cantilever beam gap		-40°C	ISO 180/1A	8.0 kJ/m²
Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	180 kJ/m²
Impact strength of simply supported beam without notch		-30°C	ISO 179/1eU	160 kJ/m²
Charpy Notched Impact Strength	23°C	ISO 179/1eA	8.0 kJ/m²
thermal performance	Test Condition	Test Method	DUPONT SHENZHEN/500P
Linear coefficient of thermal expansion	MD：-40to23°C	ISO 11359-2	9E-05 cm/cm/°C
		MD：--	ISO 11359-2	1E-04 cm/cm/°C
		TD：AnnealingTime-Optional	ISO 11359-2	30.0 min/mm
		TD：AnnealingTemperature	ISO 11359-2	160 °C
		TD：--	ISO 11359-2	1E-04 cm/cm/°C
Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	162 °C
Hot deformation temperature		1.8MPa,Unannealed	ISO 75-2/A	96.0 °C
Linear coefficient of thermal expansion	TD：-40to23°C	ISO 11359-2	9E-05 cm/cm/°C
Melting temperature		ISO 11357-3	178 °C
Electrical performance	Test Condition	Test Method	DUPONT SHENZHEN/500P
Compared to the anti leakage trace index		IEC 60112	PLC 0