Product Name / Manufacturer / Model

Grade

Certificates

Reference Price

PC TEIJIN JAPAN AD-5503

Injection grade

SGS

US$ 5,460 / MT

FOB Shenzhen Port

mechanical properties	Test Condition	Test Method	TEIJIN JAPAN/AD-5503
bending strength		ISO 178	96.0 Mpa
Tensile modulus	1mm/min	ISO 527-1 and ISO 527-2	2450 Mpa
Elongation at Break	50mm/min	ISO 527-1 and ISO 527-2	>50 %
Bending modulus	2mm/min	ISO 178	2400 Mpa
Tensile stress	50mm/min	ISO 527-1 and ISO 527-2	63 Mpa
bending strength		ASTM D790/ISO 178	/96 kg/cm²(MPa)[Lb/in²]
Impact strength of cantilever beam gap	带Notched	ISO 179	3 KJ/m
Bending modulus		ISO 178	2400 Mpa
Tensile strain	Yield	ISO 527-2/50	6.0 %
Bending modulus		ASTM D790/ISO 178	/2400 kg/cm²(MPa)[Lb/in²]
elongation		ASTM D638/ISO 527	/6 %
Tensile modulus		ISO 527-2/1	2450 Mpa
bending strength	2mm/min	ISO 178	96 Mpa
Impact strength of cantilever beam gap	没Notched	ISO 179	NB KJ/m
Tensile modulus		ASTM D638/ISO 527	/2450 kg/cm²(MPa)[Lb/in²]
tensile strength	Yield	ISO 527-2/50	63.0 Mpa
Tensile strain	Break	ISO 527-2/50	>50 %
elongation at yield	50mm/min	ISO 527-1 and ISO 527-2	6 %
tensile strength		ASTM D638/ISO 527	/63 kg/cm²(MPa)[Lb/in²]
thermal performance	Test Condition	Test Method	TEIJIN JAPAN/AD-5503
Linear coefficient of thermal expansion	Across Flow	ISO 11359-2	0.7 X10
Linear coefficient of thermal expansion			ASTM D696/ISO 11359	0.7 mm/mm.℃
Hot deformation temperature	0.45MPa	ISO 75-1 and ISO 75-2	138 °C
Vicat softening temperature		ASTM D1525/ISO R306	143 ℃（℉）
Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	124 °C
Vicat softening temperature		ISO 306/B50	143 °C
Hot deformation temperature	1.80MPa	ISO 75-1 and ISO 75-2	124 °C
Linear coefficient of thermal expansion	MD	ISO 11359-2	7E-05 cm/cm/°C
Linear coefficient of thermal expansion		Flow	ISO 11359-2	0.7 X10
Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	138 °C
Vicat softening temperature	50℃/h 50N	ISO 308	143 °C
Linear coefficient of thermal expansion	TD	ISO 11359-2	7E-05 cm/cm/°C
Electrical performance	Test Condition	Test Method	TEIJIN JAPAN/AD-5503
Dielectric strength	短时间法	IEO 60243-1	30 MV/m
Arc resistance		IEO 60112	250
Dielectric constant	1MHz	IEO 60250	3
Dissipation factor	100Hz	IEC 60250	1E-03
Dielectric constant	100Hz	IEO 60250	3.1
Dielectric loss	1MHz，Tangent	IEO 60250	90 X10
Volume resistivity		IEC 60093	>1.0E+15 ohms·cm
Dissipation factor	1MHz	IEC 60250	9E-03
Relative permittivity	100Hz	IEC 60250	3.10
Surface resistivity		IEC 60093	>1.0E+15 ohms
Relative permittivity	1MHz	IEC 60250	3.00
Dielectric strength		IEC 60243-1	30 KV/mm
Dielectric loss	100Hz，Tangent	IEO 60250	10 X10
Surface resistivity		IEO 60250	>1×10 Ω
Compared to the anti leakage trace index		IEC 60112	PLC 2
Dielectric constant		ASTM D150/IEC 60250	3
Volume resistivity		IEO 60250	>1×10 Ω.cm
Physical properties	Test Condition	Test Method	TEIJIN JAPAN/AD-5503
Water absorption rate	23°C,24hr	ISO 62	0.20 %
Shrinkage rate		ASTM D955	0.5-0.7 %
Shrinkage rate		TD:4.00mm	Internal Method	0.50-0.70 %
density		ASTM D792/ISO 1183	/1200
Water absorption rate		ASTM D570/ISO 62	0.2 %
Shrinkage rate	MD:4.00mm	Internal Method	0.50-0.70 %
Melt Volume Flow Rate (MVR)	300°C/1.2kg	ISO 1133	54.0 cm3/10min
Basic Performance	Test Condition	Test Method	TEIJIN JAPAN/AD-5503
density		ISO 1183	1200 kg/m
Refractive index		ASTM D542	1.585
Shrinkage rate	Flow	本公司制订的测定法	0.5-0.7 %
Water absorption rate	放置在23℃水中24h	ISO 62	0.2 %
Transmittance rate	试样厚度3mm	ASTM D1003	89 %
Shrinkage rate	Across Flow	本公司制订的测定法	0.5-0.7 %
Melt Volume Flow Rate (MVR)	300℃负荷1.2kg	ISO 1133	54 CM
optical performance	Test Condition	Test Method	TEIJIN JAPAN/AD-5503
transmissivity	3000μm	ASTM D1003	89.0 %
Transmittance rate		ASTM D1003/ISO 13468	89 %
Refractive index		ASTM D542/ISO 489	1.585
Refractive index			ASTM D542	1.585
impact performance	Test Condition	Test Method	TEIJIN JAPAN/AD-5503
Impact strength of simply supported beam without notch		ISO 179	NoBreak